Propiedades
Medidas
| Property | Value |
|---|---|
Diámetro | 38.1 - 101.6 mm Show Supplier Material materials with Diámetro of 38.1 - 101.6 mm |
Mecánica
| Property | Temperature | Value |
|---|---|---|
Charpy impact energy, V-notch | 23.0 °C | 310 J Show Supplier Material materials with Charpy impact energy, V-notch of 310 J |
Dureza Brinell | 23.0 °C | 200 - 241 [-] Show Supplier Material materials with Dureza Brinell of 200 - 241 [-] |
Elongación | 23.0 °C | 35 - 55 % Show Supplier Material materials with Elongación of 35 - 55 % |
Límite elástico Rp 0,2 | 23.0 °C | 345 - 400 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 345 - 400 MPa |
Resistencia a la tracción | 23.0 °C | 655 - 720 MPa Show Supplier Material materials with Resistencia a la tracción of 655 - 720 MPa |
Chemical properties
| Property | Value |
|---|---|
Azufre | 0.03 % Show Supplier Material materials with Azufre of 0.03 % |
Carbono | 0.1 % Show Supplier Material materials with Carbono of 0.1 % |
Cromo | 16 - 18 % Show Supplier Material materials with Cromo of 16 - 18 % |
Fósforo | 0.06 % Show Supplier Material materials with Fósforo of 0.06 % |
Hierro | Balance |
Manganeso | 7 - 9 % Show Supplier Material materials with Manganeso of 7 - 9 % |
Molibdeno | 0.75 % Show Supplier Material materials with Molibdeno of 0.75 % |
Nitrógeno | 0.08 - 0.18 % Show Supplier Material materials with Nitrógeno of 0.08 - 0.18 % |
Níquel | 8 - 9 % Show Supplier Material materials with Níquel of 8 - 9 % |
Silicona | 3.5 - 4.5 % Show Supplier Material materials with Silicona of 3.5 - 4.5 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applications using NITRONIC® 60 are valve stems, seats and trim, fastening systems, screening, pins, bushings and roller bearings, pump shafts and rings. Other uses include wear plates, rails guides, and bridge pins. This alloy provides a significant lower cost way to fight wear and galling compared to Nickel or Cobalt based alloys. | |
| Corrosion properties | General corrosion resistance is between AISI 304 and 316. It offers better chloride pitting resistance, stress corrosion cracking resistance and crevice corrosion resistance than AISI 316L in laboratory conditions. | |
| Heat Treatment | Annealed at 1066°C followed by water quenching. | |