Property | Temperature | Value |
---|---|---|
Charpy impact energy, V-notch | -196.0 °C | 140 J Show Supplier Material materials with Charpy impact energy, V-notch of 140 J |
Elongación | 23.0 °C | 40 % Show Supplier Material materials with Elongación of 40 % |
Límite elástico Rp 0,2 | 23.0 °C | 276 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 276 MPa |
Resistencia a la tracción | 23.0 °C | 650 MPa Show Supplier Material materials with Resistencia a la tracción of 650 MPa |
Chemical properties
Property | Value |
---|---|
Azufre | 0.01 % Show Supplier Material materials with Azufre of 0.01 % |
Carbono | 0.015 % Show Supplier Material materials with Carbono of 0.015 % |
Cobre | 1 - 1.4 % Show Supplier Material materials with Cobre of 1 - 1.4 % |
Cromo | 26 - 28 % Show Supplier Material materials with Cromo of 26 - 28 % |
Fósforo | 0.02 % Show Supplier Material materials with Fósforo of 0.02 % |
Hierro | Balance |
Manganeso | 2 % Show Supplier Material materials with Manganeso of 2 % |
Molibdeno | 6 - 7 % Show Supplier Material materials with Molibdeno of 6 - 7 % |
Nitrógeno | 0.15 - 0.25 % Show Supplier Material materials with Nitrógeno of 0.15 - 0.25 % |
Níquel | 30 - 32 % Show Supplier Material materials with Níquel of 30 - 32 % |
Silicona | 0.3 % Show Supplier Material materials with Silicona of 0.3 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications: Pulp and paper industry, flue gas desulphurization – FGD – systems, sea water heat exchangers, petroleum production and refining industry, mining industry – ore processing and pressure vessels with wall temperatures between -196°C to 550°C. | |
Corrosion properties | With excellent corrosion resistance in sulfuric acid, reducing and oxidizing media and has strong resistance to corrosion and erosion corrosion in phosphoric environment. Typically the alloy has PREN of ≥ 48, which ensure that the resistance to pitting corrosion is high. | |
Heat Treatment | Solution annealing at min 1150°C followed by water quenching. | |
Welding | Very good |