Propiedades
Medidas
| Property | Value |
|---|---|
Diámetro | 10 - 410 mm Show Supplier Material materials with Diámetro of 10 - 410 mm |
Mecánica
| Property | Temperature | Value |
|---|---|---|
Charpy impact energy, V-notch | -40.0 °C | 32 J Show Supplier Material materials with Charpy impact energy, V-notch of 32 J |
Dureza Brinell | 23.0 °C | 280 - 340 [-] Show Supplier Material materials with Dureza Brinell of 280 - 340 [-] |
Elongación | 23.0 °C | 16 % Show Supplier Material materials with Elongación of 16 % |
Límite elástico Rp 0,2 | 23.0 °C | 750 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 750 MPa |
Resistencia a la tracción | 23.0 °C | 900 - 1100 MPa Show Supplier Material materials with Resistencia a la tracción of 900 - 1100 MPa |
Chemical properties
| Property | Value |
|---|---|
Azufre | 0.005 - 0.03 % Show Supplier Material materials with Azufre of 0.005 - 0.03 % |
Carbono | 0.06 % Show Supplier Material materials with Carbono of 0.06 % |
Cromo | 15 - 17 % Show Supplier Material materials with Cromo of 15 - 17 % |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % |
Hierro | Balance |
Manganeso | 0.6 - 1.5 % Show Supplier Material materials with Manganeso of 0.6 - 1.5 % |
Molibdeno | 0.8 - 1.5 % Show Supplier Material materials with Molibdeno of 0.8 - 1.5 % |
Nitrógeno | 0.02 % Show Supplier Material materials with Nitrógeno of 0.02 % |
Níquel | 4 - 6 % Show Supplier Material materials with Níquel of 4 - 6 % |
Silicona | 0.3 - 0.7 % Show Supplier Material materials with Silicona of 0.3 - 0.7 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The alloy has been designed to resist erosion corrosion or cavitation experienced in hydraulic applications. General areas for applications: Shafts, propellers, spindles, bolts, etc. | |
| Corrosion properties | S165M is designed for application in slightly corrosive environment. Corrosion resistance is at the level of AISI 304L in most environments, however insensitive to intergranular corrosion. | |
| Heat Treatment | Austenitize and quench from 950 to 1050°C and immediate temper at 600°C for 8 hours followed by cooling in air. | |
| Welding | Good, the low carbon martensite with the finely dispersed residual austenite yields an excellent HAZ toughness in the as welded condition. Preheating to 100°C – 200°C is suggested for very thick section or when the stress concentration after cooling require it. | |