| Property | Value |
|---|---|
Densidad | 9.13 g/cm³ Show Supplier Material materials with Densidad of 9.13 g/cm³ |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | ||
Módulo elástico | 20 °C | 225 GPa Show Supplier Material materials with Módulo elástico of 225 GPa | |
250 °C | 214 GPa Show Supplier Material materials with Módulo elástico of 214 GPa | ||
500 °C | 188 GPa Show Supplier Material materials with Módulo elástico of 188 GPa | ||
Resistencia a la tracción | 860 MPa Show Supplier Material materials with Resistencia a la tracción of 860 MPa | min. |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Coeficiente de dilatación térmica | 0.0000123 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000123 1/K | 20 to 100°C |
Conductividad térmica | 9.4 W/(m·K) Show Supplier Material materials with Conductividad térmica of 9.4 W/(m·K) | |
Temperatura de fusión | 1330.0 - 1410.0 °C Show Supplier Material materials with Temperatura de fusión of 1330.0 - 1410.0 °C |
Eléctrico
| Property | Value |
|---|---|
Resistividad eléctrica | 8.800000000000001e-10 Ω·m Show Supplier Material materials with Resistividad eléctrica of 8.800000000000001e-10 Ω·m |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Azufre | 0.03 Show Supplier Material materials with Azufre of 0.03 | max. |
Carbono | 0.05 - 0.15 % Show Supplier Material materials with Carbono of 0.05 - 0.15 % | |
Cromo | 19.0 - 21.0 % Show Supplier Material materials with Cromo of 19.0 - 21.0 % | |
Fósforo | 0.04 Show Supplier Material materials with Fósforo of 0.04 | max. |
Hierro | 3.0 Show Supplier Material materials with Hierro of 3.0 | max. |
Manganeso | 1.0 - 2.0 % Show Supplier Material materials with Manganeso of 1.0 - 2.0 % | |
Níquel | 9.0 - 11.0 % Show Supplier Material materials with Níquel of 9.0 - 11.0 % | |
Silicona | 0.4 Show Supplier Material materials with Silicona of 0.4 | max. |
Wolframio | 14.0 - 16.0 % Show Supplier Material materials with Wolframio of 14.0 - 16.0 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ||
| Corrosion properties | UGI® HT605 has excellent corrosion resistance at the high temperatures found in aircraft engines. Resistance to oxidation is good when maintained intermittently at up to 870°C and continuously at up to 1090°C. This grade is highly-resistant to flaking and oxidation under extreme conditions. | |
| General machinability | HT605 alloy is machinable using conventional techniques. However, we recommend high-speed steel tools (M40 type) or carbide tools (C1, C2 or C3 type) used on rigid equipment. HT605 alloy is more difficult to machine than austenitic stainless steels (302, 304, 321, and 347 types). Generally, we suggest reducing the feed rates, cutting speeds and pass depths. Please contact our technical assistance team for further information. | |
| Other | Available products: Others on demand. | |