Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.9 g/cm³ Show Supplier Material materials with Densidad of 7.9 g/cm³ |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Creep strength 10^3 cycles | 600 °C | 190 MPa Show Supplier Material materials with Creep strength 10^3 cycles of 190 MPa | |
700 °C | 75 MPa Show Supplier Material materials with Creep strength 10^3 cycles of 75 MPa | ||
800 °C | 40 MPa Show Supplier Material materials with Creep strength 10^3 cycles of 40 MPa | ||
900 °C | 15 MPa Show Supplier Material materials with Creep strength 10^3 cycles of 15 MPa | ||
Creep strength 10^4 cycles | 600 °C | 120 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 120 MPa | 10^4 cycles |
700 °C | 36 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 36 MPa | 10^4 cycles | |
800 °C | 18 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 18 MPa | 10^4 cycles | |
900 °C | 8.5 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 8.5 MPa | 10^4 cycles | |
Creep strength 10^5 cycles | 600 °C | 65 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 65 MPa | 10^5 cycles |
700 °C | 10 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 10 MPa | 10^5 cycles | |
800 °C | 7.5 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 7.5 MPa | 10^5 cycles | |
900 °C | 3 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 3 MPa | 10^5 cycles | |
Dureza Brinell | 223.0 Show Supplier Material materials with Dureza Brinell of 223.0 | max. | |
Dureza Rockwell B | 95.0 Show Supplier Material materials with Dureza Rockwell B of 95.0 | max. | |
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | min., for 20-800°C | |
Módulo elástico | 20 °C | 196 GPa Show Supplier Material materials with Módulo elástico of 196 GPa | |
200 °C | 185 GPa Show Supplier Material materials with Módulo elástico of 185 GPa | ||
400 °C | 170 GPa Show Supplier Material materials with Módulo elástico of 170 GPa | ||
600 °C | 155 GPa Show Supplier Material materials with Módulo elástico of 155 GPa | ||
800 °C | 135 GPa Show Supplier Material materials with Módulo elástico of 135 GPa | ||
1000 °C | 120 GPa Show Supplier Material materials with Módulo elástico of 120 GPa | ||
Resistencia a la tracción | 20 °C | 550.0 - 750.0 MPa Show Supplier Material materials with Resistencia a la tracción of 550.0 - 750.0 MPa | |
100 °C | 470.0 - 670.0 MPa Show Supplier Material materials with Resistencia a la tracción of 470.0 - 670.0 MPa | ||
200 °C | 440.0 - 640.0 MPa Show Supplier Material materials with Resistencia a la tracción of 440.0 - 640.0 MPa | ||
400 °C | 400.0 - 600.0 MPa Show Supplier Material materials with Resistencia a la tracción of 400.0 - 600.0 MPa | ||
600 °C | 350.0 - 650.0 MPa Show Supplier Material materials with Resistencia a la tracción of 350.0 - 650.0 MPa | ||
800 °C | 200.0 - 400.0 MPa Show Supplier Material materials with Resistencia a la tracción of 200.0 - 400.0 MPa |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 20 °C | 500 J/(kg·K) Show Supplier Material materials with Calor específico of 500 J/(kg·K) | |
200 °C | 550 J/(kg·K) Show Supplier Material materials with Calor específico of 550 J/(kg·K) | ||
400 °C | 590 J/(kg·K) Show Supplier Material materials with Calor específico of 590 J/(kg·K) | ||
600 °C | 620 J/(kg·K) Show Supplier Material materials with Calor específico of 620 J/(kg·K) | ||
800 °C | 650 J/(kg·K) Show Supplier Material materials with Calor específico of 650 J/(kg·K) | ||
1000 °C | 670 J/(kg·K) Show Supplier Material materials with Calor específico of 670 J/(kg·K) | ||
Coeficiente de dilatación térmica | 0.0000165 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000165 1/K | 20 to 200°C | |
0.0000175 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000175 1/K | 20 to 400°C | ||
0.0000195 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000195 1/K | 20 to 100°C0 | ||
600 °C | 0.000018 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.000018 1/K | ||
800 °C | 0.0000185 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000185 1/K | ||
Conductividad térmica | 20 °C | 15 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15 W/(m·K) | |
200 °C | 17 W/(m·K) Show Supplier Material materials with Conductividad térmica of 17 W/(m·K) | ||
400 °C | 20 W/(m·K) Show Supplier Material materials with Conductividad térmica of 20 W/(m·K) | ||
600 °C | 23 W/(m·K) Show Supplier Material materials with Conductividad térmica of 23 W/(m·K) | ||
800 °C | 25 W/(m·K) Show Supplier Material materials with Conductividad térmica of 25 W/(m·K) | ||
1000 °C | 28 W/(m·K) Show Supplier Material materials with Conductividad térmica of 28 W/(m·K) |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Resistividad eléctrica | 20 °C | 0.00000085 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.00000085 Ω·m |
200 °C | 0.00000105 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.00000105 Ω·m | |
400 °C | 0.0000012 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.0000012 Ω·m | |
600 °C | 0.0000013 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.0000013 Ω·m | |
800 °C | 0.0000014 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.0000014 Ω·m | |
1000 °C | 0.00000145 Ω·m Show Supplier Material materials with Resistividad eléctrica of 0.00000145 Ω·m |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Azufre | 0.015 Show Supplier Material materials with Azufre of 0.015 | max. |
Carbono | 0.15 Show Supplier Material materials with Carbono of 0.15 | max. |
Cromo | 19.0 - 20.0 % Show Supplier Material materials with Cromo of 19.0 - 20.0 % | |
Fósforo | 0.04 Show Supplier Material materials with Fósforo of 0.04 | max. |
Manganeso | 2.0 Show Supplier Material materials with Manganeso of 2.0 | max. |
Nitrógeno | 0.1 Show Supplier Material materials with Nitrógeno of 0.1 | max. |
Níquel | 11.0 - 12.5 % Show Supplier Material materials with Níquel of 11.0 - 12.5 % | |
Silicona | 1.5 - 2.5 % Show Supplier Material materials with Silicona of 1.5 - 2.5 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ||
| Cold Forming | Bending – Forming Like other austenitic steels and heat-resistant steels, UGI® 4828 can be cold worked easily. Because UGI® 4828 is ductile, it is well suited to bending and forming. However, long-term high-temperature service may reduce the ductility of the steel. Initial ductility can be restored with a solution annealing heat treatment. | |
| Corrosion properties | UGI® 4828 has good corrosion resistance. The austenitic microstructure combined with the high silicon (≥1.5%) and chromium additions (≥ 19%) give this alloy a better high-temperature corrosion resistance than the AISI 321 or AISI 347 grades. This grade is not designed for wet corrosion resistance purposes even though, in its annealed condition, UGI® 4828 provides better corrosion resistance in a marine atmosphere than UGI® 4307 (AISI 304L). High-temperature oxidation resistance UGI® 4828 has a high destructive scaling temperature and thus exhibits good scaling resistance in both continuous and intermittent service up to 1000°C (see the chart on the right side of the material page). Typical working temperatures of UGI® 4828 in sulphur-containing gases are as follows: | |
| General machinability | In the graphs on the right side og the material page is a comparison of UGI® 4828 with UGI® 4541, UGI® 4841 and UGI® 4845 in turning with a SECO TM2000 CNMG 120408-MF4 tool, in terms of: In terms of productivity, UGI® 4828 is inferior to UGI® 4541 (mainly because of the high sulphur content of UGI® 4541) and similar to UGI® 4841 and UGI® 4845 (despite its much lower Ni content compared to these two grades). In terms of chip breakability, owing to its moderate carbon content and high silicon content, UGI® 4828 is similar to UGI® 4541, despite its lower sulphur content. It is superior to UGI®4841 and far superior to UGI® 4845, which have very low sulphur contents. | |
| Heat Treatment | Solution annealing Optimal material properties are produced after solution annealing at between 1050°C and 1150°C. This should be followed by a rapid cooling in air or water. | |
| Hot forming | Forging UGI® 4828 can be easily forged at between 800°C and 1150°C. Components should be cooled quickly, this can be done either in air or in water. Post-forging annealing heat treatment is not generally required since the material is designed for high-temperature applications. | |
| Other | Available products: Other products: contact the supplier | |
| Surface Treatment | Pickling Mechanical methods are preferred to pickling to remove oxides, slag and incrustations. Strong pickling pastes should be avoided since the welded alloy is susceptible to intergranular corrosion. | |
| Welding | UGI® 4828 has good/very good weldability. It is weldable using all the usual arc welding processes such as GMAW, GTAW, SAW and SMAW. Laser beam welding must be used with care because of its tendency to promote hot cracking in this kind of austenitic grade. No preheating is required and no post-weld heat treatment is required. Nickel-based filler materials containing Niobium are not recommended since intermetallic intergranular precipitations may occur at the fusion line. The interpass temperature should be limited to 150°C. Precautions: | |