Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.8 g/cm³ Show Supplier Material materials with Densidad of 7.8 g/cm³ |
Mecánica
| Property | Value | Comment |
|---|---|---|
Elongación | 20 % Show Supplier Material materials with Elongación of 20 % | min. |
Módulo elástico | 220 GPa Show Supplier Material materials with Módulo elástico of 220 GPa | |
Resistencia a la tracción | 500.0 - 750.0 MPa Show Supplier Material materials with Resistencia a la tracción of 500.0 - 750.0 MPa |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Coeficiente de dilatación térmica | 0.0000111 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0000111 1/K | 20 to 100°C |
Conductividad térmica | 15 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15 W/(m·K) |
Eléctrico
| Property | Value |
|---|---|
Resistividad eléctrica | 6.100000000000001e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 6.100000000000001e-07 Ω·m |
Magnético
| Property | Value | Comment |
|---|---|---|
Fuerza coercitiva | 300.0 - 400.0 A/m Show Supplier Material materials with Fuerza coercitiva of 300.0 - 400.0 A/m | Turned bar with magnetic annealing |
Permeabilidad magnética relativa | 900 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 900 [-] | Turned bar with magnetic annealing |
1100 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 1100 [-] | Turned bar with magnetic annealing | |
Polarización de saturación | 1.57 T Show Supplier Material materials with Polarización de saturación of 1.57 T | Turned bar with magnetic annealing |
Remanencia | 0.8 - 1.0 T Show Supplier Material materials with Remanencia of 0.8 - 1.0 T | Turned bar with magnetic annealing |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Azufre | 0.15 - 0.25 % Show Supplier Material materials with Azufre of 0.15 - 0.25 % | max. |
Carbono | 0.08 Show Supplier Material materials with Carbono of 0.08 | max. |
Cromo | 17.5 - 18.5 % Show Supplier Material materials with Cromo of 17.5 - 18.5 % | |
Fósforo | 0.04 Show Supplier Material materials with Fósforo of 0.04 | max. |
Manganeso | 1.0 Show Supplier Material materials with Manganeso of 1.0 | max. |
Molibdeno | 1.5 - 2.5 % Show Supplier Material materials with Molibdeno of 1.5 - 2.5 % | |
Nitrógeno | 0.07 Show Supplier Material materials with Nitrógeno of 0.07 | max. |
Silicona | 1.0 Show Supplier Material materials with Silicona of 1.0 | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ||
| Corrosion properties | Generalized corrosion in 2M sulphuric acid and at ambient temperature. Good resistance to generalized corrosion in sulphuric acid, better than that of UGI®4105. | |
| General machinability | Turning: UGI® 4114 has very good turning machinability (better than that of UGI® 4305). | |
| Heat Treatment | Softening: Maximum softening heat treatment with holding temperature of 800°C followed by air cooling. Do not exceed 825°C. | |
| Hot forming | Forging: Heated slowly to 850°C, then more quickly to 1100/1130°C. Forging between 1130°C and 750°C. | |
| Other | Available products: Contact the supplier for dimensions | |
| Surface Treatment | contact the supplier | |