Propiedades
General
| Property | Value | Comment |
|---|---|---|
Densidad | 2.75 - 2.84 g/cm³ Show Material materials with Densidad of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coeficiente de Poisson | -269.0 °C | 0.341 [-] Show Material materials with Coeficiente de Poisson of 0.341 [-] | T851 | EN 573-3 | ||
-195.0 °C | 0.355 [-] Show Material materials with Coeficiente de Poisson of 0.355 [-] | T851 | EN 573-3 | |||
27.0 °C | 0.313 [-] Show Material materials with Coeficiente de Poisson of 0.313 [-] | T851 | EN 573-3 | |||
Límite elástico | -269.0 °C | 461.3 MPa Show Material materials with Límite elástico of 461.3 MPa | T851 | EN 573-3 | RP02 | |
-195.0 °C | 413.7 MPa Show Material materials with Límite elástico of 413.7 MPa | T851 | EN 573-3 | RP02 | ||
20.0 °C | 435.0 MPa Show Material materials with Límite elástico of 435.0 MPa | T851 | EN 573-3 | Sheet | ||
27.0 °C | 361.2 MPa Show Material materials with Límite elástico of 361.2 MPa | T851 | EN 573-3 | RP02 | ||
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Módulo elástico | -269.0 °C | 82.0 GPa Show Material materials with Módulo elástico of 82.0 GPa | T851 | EN 573-3 | ||
-195.0 °C | 78.6 GPa Show Material materials with Módulo elástico of 78.6 GPa | T851 | EN 573-3 | |||
27.0 °C | 70.8 GPa Show Material materials with Módulo elástico of 70.8 GPa | T851 | EN 573-3 | |||
Plane-Strain Fracture Toughnes | 20.0 °C | 32.6 - 36.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.6 - 36.6 MPa·√m | T851 | EN 573-3 | ||
20.0 °C | 32.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.6 MPa·√m | T851 | EN 573-3 | |||
20.0 °C | 36.0 - 39.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.0 - 39.0 MPa·√m | T851 | EN 573-3 | Sheet | ||
20.0 °C | 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.0 MPa·√m | T851 | EN 573-3 | Sheet | ||
20.0 °C | 36.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.6 MPa·√m | T851 | EN 573-3 | |||
20.0 °C | 39.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 39.0 MPa·√m | T851 | EN 573-3 | Sheet | ||
Resistencia a la tracción | -269.0 °C | 663.9 MPa Show Material materials with Resistencia a la tracción of 663.9 MPa | T851 | EN 573-3 | ||
-195.0 °C | 563.9 MPa Show Material materials with Resistencia a la tracción of 563.9 MPa | T851 | EN 573-3 | |||
27.0 °C | 470.2 MPa Show Material materials with Resistencia a la tracción of 470.2 MPa | T851 | EN 573-3 |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Coeficiente de dilatación térmica | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Conductividad térmica | 112.0 - 251.0 W/(m·K) Show Material materials with Conductividad térmica of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Temperatura de fusión | 500.0 - 650.0 °C Show Material materials with Temperatura de fusión of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Eléctrico
| Property | Value | Comment |
|---|---|---|
Conductividad eléctrica | 18000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Resistividad eléctrica | 3.4e-08 - 6e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Circonio | 0.1 - 0.25 % Show Material materials with Circonio of 0.1 - 0.25 % | T851 | EN 573-3 | Sheet |
Cobre | 5.8 - 6.8 % Show Material materials with Cobre of 5.8 - 6.8 % | T851 | EN 573-3 | Sheet |
Hierro | 0.3 Show Material materials with Hierro of 0.3 | T851 | EN 573-3 | Sheet |
Magnesio | 0.02 Show Material materials with Magnesio of 0.02 | T851 | EN 573-3 | Sheet |
Manganeso | 0.2 - 0.4 % Show Material materials with Manganeso of 0.2 - 0.4 % | T851 | EN 573-3 | Sheet |
Silicona | 0.2 Show Material materials with Silicona of 0.2 | T851 | EN 573-3 | Sheet |
Titanio | 0.02 - 0.1 % Show Material materials with Titanio of 0.02 - 0.1 % | T851 | EN 573-3 | Sheet |
Vanadio | 0.05 - 0.15 % Show Material materials with Vanadio of 0.05 - 0.15 % | T851 | EN 573-3 | Sheet |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | T851 | EN 573-3 | Sheet |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |