General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 6.7 g/cm³ Show Material materials with Density of 6.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Bending Fatigue Strength | 23.0 °C | 48 MPa Show Material materials with Bending Fatigue Strength of 48 MPa | |
Elastic modulus | 20.0 °C | 85 GPa Show Material materials with Elastic modulus of 85 GPa | |
Elongation | 20.0 °C | 3 % Show Material materials with Elongation of 3 % | |
80.0 °C | 10 % Show Material materials with Elongation of 10 % | ||
150.0 °C | 21 % Show Material materials with Elongation of 21 % | ||
Elongation A50 | 20.0 °C | 10 % Show Material materials with Elongation A50 of 10 % | |
23.0 °C | 10 % Show Material materials with Elongation A50 of 10 % | ||
Hardness, Brinell | 20.0 °C | 80 - 83 [-] Show Material materials with Hardness, Brinell of 80 - 83 [-] | |
23.0 °C | 83 [-] Show Material materials with Hardness, Brinell of 83 [-] | ||
80.0 °C | 55 [-] Show Material materials with Hardness, Brinell of 55 [-] | ||
150.0 °C | 28 [-] Show Material materials with Hardness, Brinell of 28 [-] | ||
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Zinc Aluminium |
Tensile strength | 20.0 °C | 275 - 280 MPa Show Material materials with Tensile strength of 275 - 280 MPa | |
23.0 °C | 280 MPa Show Material materials with Tensile strength of 280 MPa | ||
80.0 °C | 222 MPa Show Material materials with Tensile strength of 222 MPa | ||
150.0 °C | 140 MPa Show Material materials with Tensile strength of 140 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 200 - 220 MPa Show Material materials with Yield strength Rp0.2 of 200 - 220 MPa | |
23.0 °C | 200 MPa Show Material materials with Yield strength Rp0.2 of 200 MPa | ||
80.0 °C | 160 MPa Show Material materials with Yield strength Rp0.2 of 160 MPa | ||
150.0 °C | 70 MPa Show Material materials with Yield strength Rp0.2 of 70 MPa | ||
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.2E-5 - 2.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.8E-5 1/K | Typical for Zinc Aluminium |
Melting point | 375 - 485 °C Show Material materials with Melting point of 375 - 485 °C | Typical for Zinc Aluminium | |
Specific heat capacity | 23.0 °C | 393 - 525 J/(kg·K) Show Material materials with Specific heat capacity of 393 - 525 J/(kg·K) | Typical for Zinc Aluminium |
Thermal conductivity | 20.0 °C | 113 W/(m·K) Show Material materials with Thermal conductivity of 113 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 20.0 °C | 1.51E+7 S/m Show Material materials with Electrical conductivity of 1.51E+7 S/m |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m Show Material materials with Electrical resistivity of 6.6E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Aluminium | 3.7 - 4.3 % Show Material materials with Aluminium of 3.7 - 4.3 % |
Cadmium | 5E-3 % Show Material materials with Cadmium of 5E-3 % |
Copper | 0.1 % Show Material materials with Copper of 0.1 % |
Iron | 0.05 % Show Material materials with Iron of 0.05 % |
Lead | 5E-3 % Show Material materials with Lead of 5E-3 % |
Magnesium | 0.03 - 0.06 % Show Material materials with Magnesium of 0.03 - 0.06 % |
Nickel | 0.02 % Show Material materials with Nickel of 0.02 % |
Other | Rest Zn |
Silicon | 0.03 % Show Material materials with Silicon of 0.03 % |
Tin | 2E-3 % Show Material materials with Tin of 2E-3 % |
Zinc | 95.43 % Show Material materials with Zinc of 95.43 % |