General
Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.15 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.15 [-] | max. |
Dimension
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 32 % Show Supplier Material materials with Elongation of 32 % | min. | for thickness 1.8-2 mm | Transverse, A80 |
32 % Show Supplier Material materials with Elongation of 32 % | min. | for thickness 2-3 mm | Transverse, A80 | |
37 % Show Supplier Material materials with Elongation of 37 % | min. A5.65√So | for thickness 3-13 mm | |
Tensile strength | 300 - 380 MPa Show Supplier Material materials with Tensile strength of 300 - 380 MPa | for thickness 1.8-13 mm | Transverse |
Yield strength | 200 - 310 MPa Show Supplier Material materials with Yield strength of 200 - 310 MPa | for thickness 1.8-2 mm | Transverse |
200 - 290 MPa Show Supplier Material materials with Yield strength of 200 - 290 MPa | for thickness 2-6 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.02 % Show Supplier Material materials with Aluminium of 0.02 % | min. |
Boron | 0.002 - 0.005 % Show Supplier Material materials with Boron of 0.002 - 0.005 % | |
Carbon | 0.02 - 0.08 % Show Supplier Material materials with Carbon of 0.02 - 0.08 % | |
Manganese | 0.35 % Show Supplier Material materials with Manganese of 0.35 % | max. |
Phosphorus | 0.025 % Show Supplier Material materials with Phosphorus of 0.025 % | max. |
Silicon | 0.03 % Show Supplier Material materials with Silicon of 0.03 % | max. |
Sulfur | 0.02 % Show Supplier Material materials with Sulfur of 0.02 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Structural forming grade which is well suited to applications requiring high reproducibility of processing performance (especially control of springback). That is why the S200D AM FCE grade is especially suitable for applications such as compressor casings. | |
Chemical composition | The chemical properties given are based on cast analysis data. | |
Coating | Galvanisation: Class 1 |