General
Property | Value | Comment |
---|---|---|
Carbon equivalent (CEV) | 0.4 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.4 [-] | max. |
Dimension
Property | Value |
---|---|
Dimensions | *Pickled products with thicknesses up to 15 mm may be delivered after prior agreement: please contact us. Please feel free to check the figure on the right side of the material page for more details. |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | -20 °C | 40 J Show Supplier Material materials with Charpy impact energy of 40 J | min. | for thickness 6-16 mm |
Elongation | 14 % Show Supplier Material materials with Elongation of 14 % | min. | for thickness < 3 mm | Transverse, A80 | |
15 % Show Supplier Material materials with Elongation of 15 % | min. | for thickness < 3 mm, A80 | ||
17 % Show Supplier Material materials with Elongation of 17 % | min. A5.65√So | for thickness 3-16 mm | Transverse | ||
18 % Show Supplier Material materials with Elongation of 18 % | min. A5.65√So | for thickness 3-16 mm | ||
Tensile strength | 520 - 640 MPa Show Supplier Material materials with Tensile strength of 520 - 640 MPa | for thickness < 16 mm | |
530 - 640 MPa Show Supplier Material materials with Tensile strength of 530 - 640 MPa | for thickness < 16 mm | Transverse | ||
Yield strength | 460 - 560 MPa Show Supplier Material materials with Yield strength of 460 - 560 MPa | for thickness < 16 mm | |
490 - 590 MPa Show Supplier Material materials with Yield strength of 490 - 590 MPa | for thickness < 16 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.015 % Show Supplier Material materials with Aluminium of 0.015 % | min. |
Carbon | 0.12 % Show Supplier Material materials with Carbon of 0.12 % | max. |
Manganese | 1.5 % Show Supplier Material materials with Manganese of 1.5 % | max. |
Niobium | 0.08 % Show Supplier Material materials with Niobium of 0.08 % | max. |
Phosphorus | 0.02 % Show Supplier Material materials with Phosphorus of 0.02 % | max. |
Silicon | 0.03 % Show Supplier Material materials with Silicon of 0.03 % | max. |
Sulfur | 0.012 % Show Supplier Material materials with Sulfur of 0.012 % | max. |
Titanium | 0.15 % Show Supplier Material materials with Titanium of 0.15 % | max. |
Vanadium | 0.2 % Show Supplier Material materials with Vanadium of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | High strength Amstrong® steels are used in a wide range of applications in transport (earth movers, trailers, agricultural and railroad machinery etc), profiling (racks etc) and building (cranes, safety barriers, light poles etc). Significant weight reductions can be achieved by using Amstrong® steels, especially for cranes and heavy vehicle trailers, thus allowing a larger payload. | |
Chemical composition | The chemical properties given are based on cast analysis data. | |
Coating | Galvanisation: Class 1 Suitability for hot-dip zinc coating is defined as per the requirements of EN ISO 14713-2 Table 1 and NFA 35-503. | |
Other | Toughness guarantee at -40°C: on request |