Dimension
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 40 % Show Supplier Material materials with Elongation of 40 % | min. | for thickness 0.5-3 mm | Transverse | A80 |
Plastic strain ratio | 1.5 [-] Show Supplier Material materials with Plastic strain ratio of 1.5 [-] | min. | 90ᵒ Transverse | for thickness 2-3 mm |
1.7 [-] Show Supplier Material materials with Plastic strain ratio of 1.7 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm | |
Strain hardening exponent | 0.19 [-] Show Supplier Material materials with Strain hardening exponent of 0.19 [-] | min. | 90ᵒ Transverse | for thickness 0.5-3 mm |
Tensile strength | 270 - 350 MPa Show Supplier Material materials with Tensile strength of 270 - 350 MPa | for thickness 0.5-3 mm | Transverse |
Yield strength | 90 - 160 MPa Show Supplier Material materials with Yield strength of 90 - 160 MPa | for thickness 0.5-3 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.02 % Show Supplier Material materials with Carbon of 0.02 % | max. |
Manganese | 0.5 % Show Supplier Material materials with Manganese of 0.5 % | max. |
Phosphorus | 0.03 % Show Supplier Material materials with Phosphorus of 0.03 % | max. |
Sulfur | 0.05 % Show Supplier Material materials with Sulfur of 0.05 % | max. |
Titanium | 0.2 % Show Supplier Material materials with Titanium of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | This steel has many applications: | |
Coating | Enamelling Surface preparation: Application of the enamel and firing: Finally, firing is performed at a temperature of about 830°C. | |
Joining | It can be welded without any difficulty, whatever the welding process may be. Other joining processes (clinching, crimping) may also be used. | |
Processing methods | DC07EK AM FCE, interstitial free steel (IFS) with low carbon content and excellent rheological and mechanical properties, can be used for forming very complex parts. |