General
Property | Value |
---|---|
Density | 7.6 g/cm³ Show Supplier Material materials with Density of 7.6 g/cm³ |
Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 15 % Show Supplier Material materials with Elongation of 15 % | min. | Guaranteed | Transverse | A80 |
20 - 30 % Show Supplier Material materials with Elongation of 20 - 30 % | Typical values | Transverse | A80 | |
Hardness, Vickers | 205 - 235 [-] Show Supplier Material materials with Hardness, Vickers of 205 - 235 [-] | Typical values |
Tensile strength | 590 MPa Show Supplier Material materials with Tensile strength of 590 MPa | min. | Guaranteed | Transverse |
610 - 660 MPa Show Supplier Material materials with Tensile strength of 610 - 660 MPa | Typical values | Transverse | |
Yield strength | 480 MPa Show Supplier Material materials with Yield strength of 480 MPa | min. | Guaranteed | Transverse |
495 - 545 MPa Show Supplier Material materials with Yield strength of 495 - 545 MPa | Typical values | Transverse | |
Yield to strength ratio | 0.8 - 0.85 [-] Show Supplier Material materials with Yield to strength ratio of 0.8 - 0.85 [-] | Typical values |
Magnetic
Technological properties
Property | ||
---|---|---|
Application areas | High strength values, combined with low losses and good permeability, make this grade particularly suitable for high-speed rotating machines. | |
Coating | This standard grade is available non-insulated or varnished with any of the coating types described in the following link https://industry.arcelormittal.com/catalogue/D28/EN . | |
Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |