Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 16 % Show Supplier Material materials with Elongation of 16 % | min. | for thickness 1 mm | Transverse | A80 | Guaranteed |
30 - 40 % Show Supplier Material materials with Elongation of 30 - 40 % | for thickness 1 mm | Transverse | A80 | Typical values | |
Hardness, Vickers | 130 - 160 [-] Show Supplier Material materials with Hardness, Vickers of 130 - 160 [-] | Typical values for thickness 1 mm |
Tensile strength | 325 MPa Show Supplier Material materials with Tensile strength of 325 MPa | min. | Guaranteed |
420 - 470 MPa Show Supplier Material materials with Tensile strength of 420 - 470 MPa | Typical values | |
Yield strength | 250 MPa Show Supplier Material materials with Yield strength of 250 MPa | min. | Guaranteed | Transverse |
290 - 340 MPa Show Supplier Material materials with Yield strength of 290 - 340 MPa | Typical values | Transverse | |
Yield to strength ratio | 0.68 - 0.73 [-] Show Supplier Material materials with Yield to strength ratio of 0.68 - 0.73 [-] | Typical values |
Magnetic
Property | Value | Comment |
---|---|---|
Guaranteed polarization | 1.6 [-] Show Supplier Material materials with Guaranteed polarization of 1.6 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.83 [-] Show Supplier Material materials with Guaranteed polarization of 1.83 [-] | min. | for thickness 1 mm | in DC at 15000 A/m | |
Typical polarization | 1.71 [-] Show Supplier Material materials with Typical polarization of 1.71 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.9 [-] Show Supplier Material materials with Typical polarization of 1.9 [-] | min. | for thickness 1 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |