Dimension
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mechanical
Property | Value | Comment |
---|---|---|
Elongation | 34 % Show Supplier Material materials with Elongation of 34 % | min. | for thickness 0.3-0.5 mm | Transverse | A80 |
36 % Show Supplier Material materials with Elongation of 36 % | min. | for thickness 0.5-0.7 mm | Transverse | A80 | |
38 % Show Supplier Material materials with Elongation of 38 % | min. | for thickness 0.7-3 mm | Transverse | A80 | |
Plastic strain ratio | 1.6 [-] Show Supplier Material materials with Plastic strain ratio of 1.6 [-] | min. | 90ᵒ Transverse | for thickness 2-3 mm |
1.8 [-] Show Supplier Material materials with Plastic strain ratio of 1.8 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm | |
Strain hardening exponent | 0.19 [-] Show Supplier Material materials with Strain hardening exponent of 0.19 [-] | min. | 90ᵒ Transverse | for thickness 0.5-3 mm |
Tensile strength | 270 - 350 MPa Show Supplier Material materials with Tensile strength of 270 - 350 MPa | for thickness 0.3-3 mm | Transverse |
Yield strength | 140 - 250 MPa Show Supplier Material materials with Yield strength of 140 - 250 MPa | for thickness 0.3-0.5 mm | Transverse |
140 - 230 MPa Show Supplier Material materials with Yield strength of 140 - 230 MPa | for thickness 0.5-0.7 mm | Transverse | |
140 - 210 MPa Show Supplier Material materials with Yield strength of 140 - 210 MPa | for thickness 0.7-3 mm | Transverse |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.08 % Show Supplier Material materials with Carbon of 0.08 % | max. |
Manganese | 0.4 % Show Supplier Material materials with Manganese of 0.4 % | max. |
Phosphorus | 0.025 % Show Supplier Material materials with Phosphorus of 0.025 % | max. |
Sulfur | 0.025 % Show Supplier Material materials with Sulfur of 0.025 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Electrogalvanised products are particularly suitable for industrial and domestic appliances. Some of the most common applications include: | |
Coating | ||
Other | Storage ArcelorMittal’s electrogalvanised steel is supplied passivated and/or phosphated and/or oiled to temporarily limit the risk of white rust formation. During transport and storage, all necessary precautions must be taken to keep the material dry and to prevent the formation of condensation. Rust prevention can be further improved by the application of an Easyfilm® thin organic coating. Forming and joining The forming and joining techniques mainly used for uncoated steel sheets are also suitable for steel sheet with electrogalvanised coatings, even in the case of extreme forming operations. Forming performance is improved if electrogalvanised steel is coated with an Easyfilm® thin organic coating. Painting Electrogalvanised steel can be painted after degreasing and surface treatment when supplied oiled. When phosphated or coated with an Easyfilm® thin organic coating, electrogalvanised steel can be painted directly, without any prior surface treatment. However, the paint must be compatible with the Easyfilm® resin. Mechanical properties The choice of direction for the mechanical properties should be specified when ordering. | |
Welding | In electrical resistance welding, the welding current must be suitably regulated and regularly adjusted. Electrode life can be extended by regularly stepping up the welding current and periodically dressing (machining) the electrodes. |