BMG-AT41

Alternative and trade names
BMG-AT41®
Want to keep this datasheet? Save it now in your required format

Description

The material is produced via the ingot cast route

Related Standards

Equivalent Materials

This material data has been provided by Broder Metals Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValueComment

Grain size

5 μm

Show Supplier Material materials with Grain size of 5 μm

Maximum, ASTM E112

Mechanical

PropertyTemperatureValueComment

Charpy impact energy, V-notch

23.0 °C

27 - 40 J

Show Supplier Material materials with Charpy impact energy, V-notch of 27 - 40 J

Depending on the Thickness

Creep strength

450.0 °C

520 MPa

Show Supplier Material materials with Creep strength of 520 MPa

For 10000 hours

500.0 °C

384 MPa

Show Supplier Material materials with Creep strength of 384 MPa

For 10000 hours

550.0 °C

261 MPa

Show Supplier Material materials with Creep strength of 261 MPa

For 10000 hours

600.0 °C

127 MPa

Show Supplier Material materials with Creep strength of 127 MPa

For 10000 hours

Elongation

23.0 °C

15 %

Show Supplier Material materials with Elongation of 15 %

Izod impact energy

23.0 °C

27 J

Show Supplier Material materials with Izod impact energy of 27 J

Reduction of area

23.0 °C

50 %

Show Supplier Material materials with Reduction of area of 50 %

Yield strength Rp0.2

24.0 °C

660 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 660 MPa

100.0 °C

624 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 624 MPa

150.0 °C

603 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 603 MPa

200.0 °C

595 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 595 MPa

250.0 °C

581 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 581 MPa

300.0 °C

573 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 573 MPa

350.0 °C

559 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 559 MPa

400.0 °C

537 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 537 MPa

450.0 °C

508 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 508 MPa

500.0 °C

464 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 464 MPa

600.0 °C

406 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 406 MPa

Unlock all property charts

Chemical properties

PropertyValueComment

Aluminium

0.015 - 0.08 %

Show Supplier Material materials with Aluminium of 0.015 - 0.08 %

Arsenic

0.02 %

Show Supplier Material materials with Arsenic of 0.02 %

Boron

0.001 - 0.01 %

Show Supplier Material materials with Boron of 0.001 - 0.01 %

Carbon

0.17 - 0.23 %

Show Supplier Material materials with Carbon of 0.17 - 0.23 %

Chromium

0.9 - 1.2 %

Show Supplier Material materials with Chromium of 0.9 - 1.2 %

Copper

0.2 %

Show Supplier Material materials with Copper of 0.2 %

Iron

Balance

Manganese

0.35 - 0.75 %

Show Supplier Material materials with Manganese of 0.35 - 0.75 %

Molybdenum

0.9 - 1.1 %

Show Supplier Material materials with Molybdenum of 0.9 - 1.1 %

Nickel

0.2 %

Show Supplier Material materials with Nickel of 0.2 %

Other

0.1 %

Show Supplier Material materials with Other of 0.1 %

P+2.43As+3.57Sn+8.16Sb+0.13Cu

Phosphorus

0.02 %

Show Supplier Material materials with Phosphorus of 0.02 %

Silicon

0.4 %

Show Supplier Material materials with Silicon of 0.4 %

Sulfur

0.08 %

Show Supplier Material materials with Sulfur of 0.08 %

Tin

0.02 %

Show Supplier Material materials with Tin of 0.02 %

Titanium

0.07 - 0.15 %

Show Supplier Material materials with Titanium of 0.07 - 0.15 %

Vanadium

0.6 - 0.8 %

Show Supplier Material materials with Vanadium of 0.6 - 0.8 %

Technological properties

Property
Application areas

Fasteners with specified elevated and/or low temperature properties.