Properties
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Charpy impact energy, V-notch | -20 °C | 27 J Show Supplier Material materials with Charpy impact energy, V-notch of 27 J | *The specified values are minimum values for the average of 3 tests. No individual value is to be less than 70 % of the specified minimum. For plate thickness below 11 mm the test can be carried out on Charpy-V specimens or Charpy-V-type specimens with reduced width. The minimum impact value will be reduced proportionally to the reduction of the specimen’s cross section | |
0 °C | 34 J Show Supplier Material materials with Charpy impact energy, V-notch of 34 J | * | ||
Creep strength 10^4 cycles | 400 °C | 324 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 324 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | |
400 °C | 402 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 402 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
410 °C | 315 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 315 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
410 °C | 385 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 385 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
420 °C | 306 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 306 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
420 °C | 368 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 368 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
430 °C | 295 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 295 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
430 °C | 348 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 348 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
440 °C | 281 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 281 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
440 °C | 328 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 328 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
450 °C | 265 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 265 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
450 °C | 304 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 304 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
460 °C | 239 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 239 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
460 °C | 274 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 274 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
470 °C | 212 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 212 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
470 °C | 242 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 242 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
480 °C | 180 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 180 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
480 °C | 212 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 212 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
490 °C | 145 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 145 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
490 °C | 179 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 179 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
500 °C | 108 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 108 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^4 cycles | ||
500 °C | 147 MPa Show Supplier Material materials with Creep strength 10^4 cycles of 147 MPa | rupture strength | average of the scatter band known to date., 10^4 cycles | ||
Creep strength 10^5 cycles | 400 °C | 294 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 294 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | |
400 °C | 373 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 373 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
410 °C | 279 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 279 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
410 °C | 349 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 349 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
420 °C | 263 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 263 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
420 °C | 325 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 325 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
430 °C | 245 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 245 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
430 °C | 300 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 300 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
440 °C | 227 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 227 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
440 °C | 273 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 273 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
450 °C | 206 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 206 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
450 °C | 245 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 245 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
460 °C | 180 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 180 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
460 °C | 210 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 210 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
470 °C | 151 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 151 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
470 °C | 175 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 175 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
480 °C | 120 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 120 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
480 °C | 139 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 139 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
490 °C | 84 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 84 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
490 °C | 104 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 104 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
500 °C | 49 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 49 MPa | Strength for 1% (plastic) creep strain | average of the scatter band known to date., 10^5 cycles | ||
500 °C | 69 MPa Show Supplier Material materials with Creep strength 10^5 cycles of 69 MPa | rupture strength | average of the scatter band known to date., 10^5 cycles | ||
Elongation | 16 % Show Supplier Material materials with Elongation of 16 % | min. for plate thickenss t ≤ 250 mm | transverse specimens (ambient temp.), A5 | ||
Tensile strength | 580 - 740 MPa Show Supplier Material materials with Tensile strength of 580 - 740 MPa | for plate thickness 150 < t ≤ 250 mm | transverse specimens (ambient temp.) | ||
590 - 740 MPa Show Supplier Material materials with Tensile strength of 590 - 740 MPa | for plate thickness 100 < t ≤ 150 mm | transverse specimens (ambient temp.) | |||
600 - 760 MPa Show Supplier Material materials with Tensile strength of 600 - 760 MPa | for plate thickness 60 < t ≤ 100 mm | transverse specimens (ambient temp.) | |||
610 - 780 MPa Show Supplier Material materials with Tensile strength of 610 - 780 MPa | for plate thickness t ≤ 60 mm | transverse specimens (ambient temp.) | |||
Yield strength | 400 MPa Show Supplier Material materials with Yield strength of 400 MPa | min. ReH for plate thickness 200 < t ≤ 250 mm | transverse specimens (ambient temp.) | ||
410 MPa Show Supplier Material materials with Yield strength of 410 MPa | min. ReH for plate thickness 150 < t ≤ 200 mm | transverse specimens (ambient temp.) | |||
420 MPa Show Supplier Material materials with Yield strength of 420 MPa | min. ReH for plate thickness 100 < t ≤ 150 mm | transverse specimens (ambient temp.) | |||
430 MPa Show Supplier Material materials with Yield strength of 430 MPa | min. ReH for plate thickness 60 < t ≤ 100 mm | transverse specimens (ambient temp.) | |||
440 MPa Show Supplier Material materials with Yield strength of 440 MPa | min. ReH for plate thickness 40 < t ≤ 60 mm | transverse specimens (ambient temp.) | |||
460 MPa Show Supplier Material materials with Yield strength of 460 MPa | min. ReH for plate thickness t ≤ 40 mm | transverse specimens (ambient temp.) | |||
100 °C | 373 MPa Show Supplier Material materials with Yield strength of 373 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
100 °C | 382 MPa Show Supplier Material materials with Yield strength of 382 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
100 °C | 392 MPa Show Supplier Material materials with Yield strength of 392 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
100 °C | 401 MPa Show Supplier Material materials with Yield strength of 401 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
100 °C | 410 MPa Show Supplier Material materials with Yield strength of 410 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
100 °C | 429 MPa Show Supplier Material materials with Yield strength of 429 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
150 °C | 361 MPa Show Supplier Material materials with Yield strength of 361 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
150 °C | 370 MPa Show Supplier Material materials with Yield strength of 370 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
150 °C | 379 MPa Show Supplier Material materials with Yield strength of 379 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
150 °C | 388 MPa Show Supplier Material materials with Yield strength of 388 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
150 °C | 397 MPa Show Supplier Material materials with Yield strength of 397 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
150 °C | 415 MPa Show Supplier Material materials with Yield strength of 415 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
200 °C | 350 MPa Show Supplier Material materials with Yield strength of 350 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
200 °C | 359 MPa Show Supplier Material materials with Yield strength of 359 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
200 °C | 368 MPa Show Supplier Material materials with Yield strength of 368 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
200 °C | 377 MPa Show Supplier Material materials with Yield strength of 377 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
200 °C | 385 MPa Show Supplier Material materials with Yield strength of 385 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
200 °C | 403 MPa Show Supplier Material materials with Yield strength of 403 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
250 °C | 340 MPa Show Supplier Material materials with Yield strength of 340 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
250 °C | 349 MPa Show Supplier Material materials with Yield strength of 349 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
250 °C | 357 MPa Show Supplier Material materials with Yield strength of 357 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
250 °C | 366 MPa Show Supplier Material materials with Yield strength of 366 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
250 °C | 374 MPa Show Supplier Material materials with Yield strength of 374 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
250 °C | 391 MPa Show Supplier Material materials with Yield strength of 391 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
300 °C | 330 MPa Show Supplier Material materials with Yield strength of 330 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
300 °C | 338 MPa Show Supplier Material materials with Yield strength of 338 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
300 °C | 347 MPa Show Supplier Material materials with Yield strength of 347 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
300 °C | 355 MPa Show Supplier Material materials with Yield strength of 355 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
300 °C | 363 MPa Show Supplier Material materials with Yield strength of 363 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
300 °C | 380 MPa Show Supplier Material materials with Yield strength of 380 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
350 °C | 318 MPa Show Supplier Material materials with Yield strength of 318 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
350 °C | 327 MPa Show Supplier Material materials with Yield strength of 327 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
350 °C | 335 MPa Show Supplier Material materials with Yield strength of 335 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
350 °C | 342 MPa Show Supplier Material materials with Yield strength of 342 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
350 °C | 350 MPa Show Supplier Material materials with Yield strength of 350 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
350 °C | 366 MPa Show Supplier Material materials with Yield strength of 366 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
400 °C | 305 MPa Show Supplier Material materials with Yield strength of 305 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 200 < t ≤ 250 mm | transverse specimens | |
400 °C | 313 MPa Show Supplier Material materials with Yield strength of 313 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
400 °C | 320 MPa Show Supplier Material materials with Yield strength of 320 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
400 °C | 328 MPa Show Supplier Material materials with Yield strength of 328 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
400 °C | 335 MPa Show Supplier Material materials with Yield strength of 335 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
400 °C | 351 MPa Show Supplier Material materials with Yield strength of 351 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens | |
450 °C | 288 MPa Show Supplier Material materials with Yield strength of 288 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 250 mm | transverse specimens | |
450 °C | 295 MPa Show Supplier Material materials with Yield strength of 295 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 150 < t ≤ 200 mm | transverse specimens | |
450 °C | 302 MPa Show Supplier Material materials with Yield strength of 302 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 100 < t ≤ 150 mm | transverse specimens | |
450 °C | 309 MPa Show Supplier Material materials with Yield strength of 309 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 60 < t ≤ 100 mm | transverse specimens | |
450 °C | 317 MPa Show Supplier Material materials with Yield strength of 317 MPa | EN 10028-2 | min. Rp0.2 for plate thickness 40 < t ≤ 60 mm | transverse specimens | |
450 °C | 331 MPa Show Supplier Material materials with Yield strength of 331 MPa | EN 10028-2 | min. Rp0.2 for plate thickness t ≤ 40 mm | transverse specimens |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Aluminium | 0.01 % Show Supplier Material materials with Aluminium of 0.01 % | min. tot. product | |
0.015 % Show Supplier Material materials with Aluminium of 0.015 % | min. tot. heat | ||
Carbon | 0.17 % Show Supplier Material materials with Carbon of 0.17 % | max. heat | |
0.19 % Show Supplier Material materials with Carbon of 0.19 % | max. product | ||
Chromium | 0.3 % Show Supplier Material materials with Chromium of 0.3 % | max. heat | |
0.35 % Show Supplier Material materials with Chromium of 0.35 % | max. product | ||
Copper | 0.4 - 0.9 % Show Supplier Material materials with Copper of 0.4 - 0.9 % | product | |
0.5 - 0.8 % Show Supplier Material materials with Copper of 0.5 - 0.8 % | heat | ||
Iron | Balance | ||
Manganese | 0.75 - 1.3 % Show Supplier Material materials with Manganese of 0.75 - 1.3 % | product | |
0.8 - 1.2 % Show Supplier Material materials with Manganese of 0.8 - 1.2 % | heat | ||
Molybdenum | 0.22 - 0.54 % Show Supplier Material materials with Molybdenum of 0.22 - 0.54 % | product | |
0.25 - 0.5 % Show Supplier Material materials with Molybdenum of 0.25 - 0.5 % | heat | ||
Nickel | 0.9 - 1.4 % Show Supplier Material materials with Nickel of 0.9 - 1.4 % | product | |
1 - 1.3 % Show Supplier Material materials with Nickel of 1 - 1.3 % | heat | ||
Niobium | 0.005 - 0.055 % Show Supplier Material materials with Niobium of 0.005 - 0.055 % | product | |
0.015 - 0.045 % Show Supplier Material materials with Niobium of 0.015 - 0.045 % | heat | ||
Nitrogen | 0.02 % Show Supplier Material materials with Nitrogen of 0.02 % | max. heat | |
0.022 % Show Supplier Material materials with Nitrogen of 0.022 % | max. product | ||
Phosphorus | 0.025 % Show Supplier Material materials with Phosphorus of 0.025 % | max. heat | |
0.03 % Show Supplier Material materials with Phosphorus of 0.03 % | max. product | ||
Silicon | 0.2 - 0.56 % Show Supplier Material materials with Silicon of 0.2 - 0.56 % | product | |
0.25 - 0.5 % Show Supplier Material materials with Silicon of 0.25 - 0.5 % | heat | ||
Sulfur | 0.01 % Show Supplier Material materials with Sulfur of 0.01 % | max. heat | |
0.013 % Show Supplier Material materials with Sulfur of 0.013 % | max. product | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Boilers in accordance with EN 12952/ EN12953 (TRD 101) for temperatures up to 500 °C. Pressure vessels in accordance with AD 2000-Merkblatt W1, HP 8/1, EN 13445 and CODAP 2005 for temperatures from -20 °C up to 500 °C. | |
| Cold Forming | DIWA 373 can be cold formed according to the general procedures. CEN/TR 10347 (Guidance for forming of structural steels in processing) as well as the provisions of VdTÜV-material data sheet 377/1 shall be observed. | |
| Delivery condtion | Delivery condition: thicknesses ≤ 100 mm normalized and tempered thicknesses > 100 mm normalized and tempered or water quenched and tempered In accordance with EN 10028-2 a water quenching and tempering treatment is already possible for thick- nesses equal or superior to 100 mm. If the heat treatment is to be performed during processing, the plates can be delivered in the normalized condition, and in exceptional cases in the as rolled condition by special agreement before the order. In this case testing of the mechanical properties is provided on the basis of simulated heat treated specimens. | |
| Flame cutting and welding | DIWA 373 can be welded and flame cut according to the general procedures. The guidelines given in EN 1011 (Welding), as well as the provisions of VdTÜV-material data sheet 377/1 shall be observed. | |
| General note | If special requirements, which are not listed in this material specification, are to be met by the steel due to its intended use or processing, these requirements are to be agreed before the order. The indications in this data sheet are product descriptions. This data sheet is updated if necessary. The current version is available from the mill or as download at www.dillinger.de. | |
| Heat Treatment | ||
| Hot forming | DIWA 373 can be hot formed according to the general procedures. CEN/TR 10347 (Guidance for forming of structural steels in processing) as well as the provisions of VdTÜV-material data sheet 377/1 shall be observed. | |
| Processing history | Fully killed, fine grained steel with metallurgical treatment in the ladle. | |
| Processing methods | The entire processing and application techniques are of fundamental importance to the reliability of the products made from this steel. The user should ensure that his design, construction and processing meth- ods are aligned with the material, correspond to the state-of-the-art that the fabricator has to comply with and are suitable for the intended use. The customer is responsible for the selection of the material. The recommendations in accordance with EN 1011-2 should be observed. | |
| Surface condition | Surface condition: Unless otherwise agreed, the provisions in accordance with class B2 of EN 10163-2 are applicable. | |
| Testings | Sampling, testing method and tests are in accordance with the provisions in EN 10028. For orders in accor- dance with VdTÜV material data sheet 377/1, the conditions indicated there are respected. Additional tests can be agreed upon. The plates are delivered with inspection certificate 3.1 or 3.2 in accordance with EN 10204. The document type and, in case of inspection certificate 3.2, the inspection representative are to be stated on the order. Tensile test at ambient temperature (transverse test specimens), Tensile test at elevated temperature (transverse specimens in accordance with 10028-2) For plate thicknesses ≥ 15 mm, the fulfilment of one of the three quality classes Z15, Z25 or Z35 in accordance with EN 10164 or similar standards can be stipulated on the order. | |
| Tolerances | Tolerances: Unless otherwise agreed, tolerances are in accordance with EN 10029, with class B for the thickness and class N for the flatness. | |