General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 3.3 g/cm³ Show Supplier Material materials with Density of 3.3 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 2500 MPa Show Supplier Material materials with Compressive strength of 2500 MPa |
Elastic modulus | 23.0 °C | 320 GPa Show Supplier Material materials with Elastic modulus of 320 GPa |
Flexural strength | 23.0 °C | 350 MPa Show Supplier Material materials with Flexural strength of 350 MPa |
Hardness, Vickers | 23.0 °C | 969 [-] Show Supplier Material materials with Hardness, Vickers of 969 [-] |
Poisson's ratio | 23.0 °C | 0.24 [-] Show Supplier Material materials with Poisson's ratio of 0.24 [-] |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.8E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.8E-6 1/K |
Specific heat capacity | 23.0 °C | 740 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 740 J/(kg·K) |
Thermal conductivity | 23.0 °C | 170 W/(m·K) Show Supplier Material materials with Thermal conductivity of 170 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Dielectric constant | 23.0 °C | 8.56 [-] Show Supplier Material materials with Dielectric constant of 8.56 [-] |
Dielectric strength | 23.0 °C | 15 kV/mm Show Supplier Material materials with Dielectric strength of 15 kV/mm |
Electrical resistivity | 23.0 °C | 1.00E+16 Ω·m Show Supplier Material materials with Electrical resistivity of 1.00E+16 Ω·m |
Loss tangent | 23.0 °C | 2.8E-4 [-] Show Supplier Material materials with Loss tangent of 2.8E-4 [-] |
Technological properties
Property | ||
---|---|---|
Application areas | Aluminum Nitride Ceramics is ideal for applications where heat dissipation is required. In addition, since it offers a coefficient of thermal expansion (CTE) near that of silicon, and excellent plasma resistance, it is used for: Semiconductor processing equipment components, Ceramic Heat-sinks for high power system, Crucible for Metal Melting, Ceramic Rod, Ceramic Heater, Ceramic Substrate | |
Processing methods | Ceramic Injection Molding, Low Pressure Injection Molding, Cold Isostatic Press, Dry Press, Tape Casting, Precision Machining Processing |