Zytel® HTN53G60LRHF BK083

Alternative and trade names
PA-GF60
Want to keep this datasheet? Save it now in your required format

Description

Zytel® HTN high performance polyamide resins feature high retention of properties upon exposure to elevated temperature, to high moisture, and to harsh chemical environments. Polymer families and grades of Zytel® HTN are tailored to optimize performance as well as processability. Typical applications with Zytel® HTN include demanding applications in the automotive, electrical and electronics, domestic appliances, and construction industries. Zytel® HTN53G60LRHF BK083 is a 60% glass reinforced, lubricated, high performance polyamide resin with improved flow. It was developed for structural applications requiring excellent surface appearance using water-heated molds.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.72 g/cm³

Show Material materials with Density of 1.72 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

21 GPa

Show Material materials with Elastic modulus of 21 GPa

ISO 527-1/-2

Elongation

23.0 °C

2.2 %

Show Material materials with Elongation of 2.2 %

ISO 527-1/-2

Flexural modulus

23.0 °C

19.1 GPa

Show Material materials with Flexural modulus of 19.1 GPa

ISO 178

Flexural strength

23.0 °C

405 MPa

Show Material materials with Flexural strength of 405 MPa

ISO 178

Impact strength, Charpy notched

-6.0 °C

17 kJ/m²

Show Material materials with Impact strength, Charpy notched of 17 kJ/m²

ISO 179/1eA

23.0 °C

16 kJ/m²

Show Material materials with Impact strength, Charpy notched of 16 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

90 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

ISO 179/1eU

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Tensile strength

23.0 °C

265 MPa

Show Material materials with Tensile strength of 265 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

255 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

245 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 245 °C

ISO 75-1/-2

Melting point

260 °C

Show Material materials with Melting point of 260 °C

ISO 11357-1/-3 | first heat

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Material materials with Shrinkage of 0.1 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.5 %

Show Material materials with Shrinkage, transverse of 0.5 %

ISO 294-4, 2577

Technological properties

Property
Fillers

60% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Min. mold temperature: 90°C, Max. mold temperature: 110°C