Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.44 g/cm³ Show Material materials with Density of 1.44 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.2 % Show Material materials with Water absorption of 1.2 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12 GPa Show Material materials with Elastic modulus of 12 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.5 % Show Material materials with Elongation of 3.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 11 GPa Show Material materials with Flexural modulus of 11 GPa | ISO 178 |
Flexural strength | 23.0 °C | 300 MPa Show Material materials with Flexural strength of 300 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA |
-6.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU |
-6.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU | |
23.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 210 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75-1/-2 | |||
Melting point | 220 °C Show Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |