Zytel® HTN51G35HSLR BK420J

Want to keep this datasheet? Save it now in your required format

Description

Zytel® HTN51G35HSLR BK420J is a 35% glass reinforced, heat stabilized, lubricated, hydrolysis resistant high performance polyamide resin with improved surface appearance. It is also a PPA resin.

Equivalent Materials

ISO 16396-PA6T

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.46 g/cm³ Show Material materials with Density of 1.46 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	11.5 GPa Show Material materials with Elastic modulus of 11.5 GPa	ISO 527-1/-2
Elongation	23.0 °C	2.6 % Show Material materials with Elongation of 2.6 %	ISO 527-1/-2
Flexural modulus	23.0 °C	10.3 GPa Show Material materials with Flexural modulus of 10.3 GPa	ISO 178
Impact strength, Charpy notched	23.0 °C	11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m²	ISO 179/1eA
Poisson's ratio	23.0 °C	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]
Tensile strength	23.0 °C	215 MPa Show Material materials with Tensile strength of 215 MPa	ISO 527-1/-2

Thermal

Property	Value	Comment
Glass transition temperature	135 °C Show Material materials with Glass transition temperature of 135 °C	ISO 11357-1/-2 \| 18°F/min
Heat deflection temperature, 1.80 MPa	264 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 264 °C	ISO 75-1/-2
Flammability	FMVSS Class: B -, Burning rate, Thickness 1 mm: 23 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.2 % Show Material materials with Shrinkage of 0.2 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	0.5 % Show Material materials with Shrinkage, transverse of 0.5 %	ISO 294-4, 2577

Technological properties

Property
Fillers	35% Glass Fiber
Processing methods	Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C

Zytel® HTN51G35HSLR BK420J

Description

Equivalent Materials

Ashby charts

Suggested reading

Properties