Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.44 g/cm³ Show Material materials with Density of 8.44 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 179 GPa Show Material materials with Elastic modulus of 179 GPa |
Elongation | 23.0 °C | 14 - 20 % Show Material materials with Elongation of 14 - 20 % |
Hardness, Rockwell C | 23.0 °C | 27 - 35 [-] Show Material materials with Hardness, Rockwell C of 27 - 35 [-] |
Tensile strength | 23.0 °C | 970 - 1000 MPa Show Material materials with Tensile strength of 970 - 1000 MPa |
Yield strength Rp0.2 | 23.0 °C | 690 - 760 MPa Show Material materials with Yield strength Rp0.2 of 690 - 760 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.34E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.34E-5 1/K |
Melting point | 1315 - 1350 °C Show Material materials with Melting point of 1315 - 1350 °C | |
Thermal conductivity | 23.0 °C | 17.5 W/(m·K) Show Material materials with Thermal conductivity of 17.5 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Specific Electrical conductivity | 28 % IACS Show Material materials with Specific Electrical conductivity of 28 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 2.3 - 3.15 % Show Material materials with Aluminium of 2.3 - 3.15 % | |
Copper | 27 - 33 % Show Material materials with Copper of 27 - 33 % | |
Iron | 2 % Show Material materials with Iron of 2 % | max. |
Nickel | 63 % Show Material materials with Nickel of 63 % | min., (Ni+Co) |
Titanium | 0.35 - 0.85 % Show Material materials with Titanium of 0.35 - 0.85 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Offshore & marine: Marine propeller shafts, pump shafts, impellers, valve trim, drill collars, high strength fasteners and bolting;Other: Oil well surveying equipment, cryogenic equipment springs and electronic components | |
| Cold Forming | It can be cold worked | |
| Corrosion properties | Excellent corrosion resistance in marine environments | |
| General machinability | It is readily machinable | |
| Hot forming | It can be hot worked | |