General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.18 g/cm³ Show Material materials with Density of 8.18 g/cm³ |
Dimension
Property | Value | Comment | |
---|---|---|---|
Diameter | 3.2 - 101.6 mm Show Material materials with Diameter of 3.2 - 101.6 mm | ||
Length | 3050 - 3660 mm Show Material materials with Length of 3050 - 3660 mm | Mill random length | |
Dimensions | Available diameters: 3.2mm, 3.6mm, 4.8mm, 6.4mm, 9.5mm, 10.5mm, 12.7mm, 15.9mm, 19.1mm, 20.6mm, 22.2mm, 25.4mm, 28.6mm, 38.1mm, 41.3mm, 44.5mm, 50.8mm, 63.5mm, 76.2mm, 101.6mm |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 166 GPa Show Material materials with Elastic modulus of 166 GPa | |
Elongation | 23.0 °C | 40 % Show Material materials with Elongation of 40 % | in 2 in. |
Hardness, Rockwell B | 23.0 °C | 80 [-] Show Material materials with Hardness, Rockwell B of 80 [-] | |
Tensile strength | 23.0 °C | 518 MPa Show Material materials with Tensile strength of 518 MPa | |
Yield strength | 23.0 °C | 159 MPa Show Material materials with Yield strength of 159 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 450.0 °C | 9E-6 1/K Show Material materials with Coefficient of thermal expansion of 9E-6 1/K | from 20°C to the mentioned temperature |
Melting point | 1427 °C Show Material materials with Melting point of 1427 °C | ||
Specific heat capacity | 23.0 °C | 502 J/(kg·K) Show Material materials with Specific heat capacity of 502 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 13 W/(m·K) Show Material materials with Thermal conductivity of 13 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 4.9E-7 Ω·m Show Material materials with Electrical resistivity of 4.9E-7 Ω·m |
Magnetic
Property | Temperature | Value |
---|---|---|
Coercive force | 23.0 °C | 4.77 A/m Show Material materials with Coercive force of 4.77 A/m |
Curie temperature | 450 °C Show Material materials with Curie temperature of 450 °C | |
Relative magnetic permeability | 23.0 °C | 100000 [-] Show Material materials with Relative magnetic permeability of 100000 [-] |
Saturation induction | 23.0 °C | 1.5 T Show Material materials with Saturation induction of 1.5 T |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | Common applications of EFI ALLOY 50 are: LF power transducers, stepping motors, magnetic shielding, solenoid cores, relay parts, magnetic valves |