ОоА Epoxy B180

Want to keep this datasheet? Save it now in your required format


В180 is a prepreg based on epoxy resin and reinforcing filler (unidirectional tapes or fabrics of various weaving) for producing details with operating temperatures up to 150°C. Out-of-autoclave prepreg technology has the most advantages of autoclave. The autoclave is not required for processing the prepreg B180. Curing takes place in a vacuum bag, with the technology of the package laminating slightly different from the vacuum infusion. It shows the following features and properties:

  • High mechanical performance
  • Possibility of application in loaded parts at service temperatures up to 120°C
  • Less stringent requirements for working staff
  • Glass transition temperature 154°C
  • Out of autoclave processing
  • This material data has been provided by Matmatch.

    All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
    Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

    Ashby charts




    Water absorption

    23.0 °C

    4.17 %

    Show Material materials with Water absorption of 4.17 %

    for 54h to boiling water



    Flexural strength

    23.0 °C

    162 MPa

    Show Material materials with Flexural strength of 162 MPa

    ASTM D790

    Plane-Strain Fracture Toughnes

    23.0 °C

    1.88 MPa·√m

    Show Material materials with Plane-Strain Fracture Toughnes of 1.88 MPa·√m

    ASTM D5045

    Tensile strength

    23.0 °C

    94 MPa

    Show Material materials with Tensile strength of 94 MPa

    ASTM D638

    Strain energy release

    ASTM D5045



    Glass transition temperature

    175 °C

    Show Material materials with Glass transition temperature of 175 °C

    ASTM E2092

    Technological properties

    Application areas

    Marine: The shells of boats and sport catamarans can be made of composites;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite

    Processing methods

    Holding at a temperature of 25-30°C, for 12 hours, a vacuum of -1 bar. Heating 2°C/min. up to 120°C, holding at 120°C for 180 minutes. Heating 2°C/min. up to 180°C, holding at 180°C for 180 minutes, cooling no faster than 5°C/min. up to 50°С.