General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Water absorption | 23.0 °C | 4.05 % Show Material materials with Water absorption of 4.05 % | for 54h to boiling water |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 4.4 GPa Show Material materials with Elastic modulus of 4.4 GPa | ASTM D638 | ||
Flexural modulus | 23.0 °C | 4.5 GPa Show Material materials with Flexural modulus of 4.5 GPa | ASTM D790 | ||
Flexural strength | 23.0 °C | 164 MPa Show Material materials with Flexural strength of 164 MPa | ASTM D790 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 1.07 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 1.07 MPa·√m | ASTM D5045 | ||
Tensile strength | 23.0 °C | 92 MPa Show Material materials with Tensile strength of 92 MPa | ASTM D638 | ||
Strain energy release | ASTM D5045 | ||||
Thermal
Magnetic
| Property | Value |
|---|---|
Curie temperature | 190 °C Show Material materials with Curie temperature of 190 °C |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Molding mode: 1)Heat 2°С/min to 145°С, vacuum –1bar, pressure 0 bar, 2)Hold at 145°C for 120 min, vacuum -1 bar, pressure 0 bar 3)Heat 2°C/min to 180°C, pressurize 5.5 bar, release vacuum 4)Hold at 180°C for 240 minutes, pressure 5.5 bar 5)Cool no faster than 5°C/min to 60°C, pressure 5.5 bar. Post-curing cycle: 1)Post-cure of the part can be carried out without a tooling, 2)Heat at rate 2°C/min to 180°C, 3)Heat no faster than 0.2°C/min to 230°C, 4)Holding at 230°C for 300min, 5)Cooling is not faster than 5°C/min to 25°C, 6)To achieve heat resistance up to 250°C, additional post-curing is required at 250°C for 240 minutes, 7)Heat from 230°C to 250°C at rate 2°C/min. | |