Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20.0 °C | 4.43 g/cm³ Show Material materials with Density of 4.43 g/cm³ | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Elastic modulus | -269.0 °C | 119.6 GPa Show Material materials with Elastic modulus of 119.6 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 118.2 GPa Show Material materials with Elastic modulus of 118.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
20.0 °C | 110.0 GPa Show Material materials with Elastic modulus of 110.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 109.2 GPa Show Material materials with Elastic modulus of 109.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
200.0 °C | 98.0 GPa Show Material materials with Elastic modulus of 98.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
400.0 °C | 84.0 GPa Show Material materials with Elastic modulus of 84.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Elongation | 20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
Hardness, Brinell | 20.0 °C | 310.0 Show Material materials with Hardness, Brinell of 310.0 | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod |
Poisson's ratio | -269.0 °C | 0.311 [-] Show Material materials with Poisson's ratio of 0.311 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 0.327 [-] Show Material materials with Poisson's ratio of 0.327 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 0.333 [-] Show Material materials with Poisson's ratio of 0.333 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Reduction of area | 20.0 °C | 15.0 % Show Material materials with Reduction of area of 15.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
20.0 °C | 20.0 % Show Material materials with Reduction of area of 20.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging | |
Shear modulus | 20.0 °C | 43.0 GPa Show Material materials with Shear modulus of 43.0 GPa | Artificially Aged | WL 3.7164-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Forging, Rod |
Tensile strength | 20.0 °C | 1060.0 MPa Show Material materials with Tensile strength of 1060.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging |
20.0 °C | 1070.0 MPa Show Material materials with Tensile strength of 1070.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging | |
20.0 °C | 1100.0 MPa Show Material materials with Tensile strength of 1100.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging, Rod | |
20.0 °C | 1180.0 MPa Show Material materials with Tensile strength of 1180.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
100.0 °C | 1090.0 MPa Show Material materials with Tensile strength of 1090.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
200.0 °C | 1000.0 MPa Show Material materials with Tensile strength of 1000.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
300.0 °C | 910.0 MPa Show Material materials with Tensile strength of 910.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
400.0 °C | 855.0 MPa Show Material materials with Tensile strength of 855.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
500.0 °C | 735.0 MPa Show Material materials with Tensile strength of 735.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coefficient of thermal expansion of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Melting point | 1500.0 - 1750.0 °C Show Material materials with Melting point of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | ||||
Specific heat capacity | 370.0 - 674.0 J/(kg·K) Show Material materials with Specific heat capacity of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Thermal conductivity | 20.0 °C | 7.12 W/(m·K) Show Material materials with Thermal conductivity of 7.12 W/(m·K) | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | 20.0 °C | 1.71e-06 Ω·m Show Material materials with Electrical resistivity of 1.71e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 5.5 - 6.75 % Show Material materials with Aluminium of 5.5 - 6.75 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Carbon | 0.08 Show Material materials with Carbon of 0.08 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Hydrogen | 0.015 Show Material materials with Hydrogen of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Iron | 0.3 Show Material materials with Iron of 0.3 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Nitrogen | 0.05 Show Material materials with Nitrogen of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Oxygen | 0.2 Show Material materials with Oxygen of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Titanium | 87.7 % Show Material materials with Titanium of 87.7 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Vanadium | 3.5 - 4.5 % Show Material materials with Vanadium of 3.5 - 4.5 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |