General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 6.8 - 7.8 g/cm³ Show Material materials with Density of 6.8 - 7.8 g/cm³ | Typical for Cast Iron |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 152 GPa Show Material materials with Elastic modulus of 152 GPa | |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | |
Hardness, HBW | 23.0 °C | 241 - 302 [-] Show Material materials with Hardness, HBW of 241 - 302 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] | Typical for Cast Iron |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Tensile strength | 23.0 °C | 700 MPa Show Material materials with Tensile strength of 700 MPa | |
Yield strength | 23.0 °C | 425 - 450 MPa Show Material materials with Yield strength of 425 - 450 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 527 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 527 J/(kg·K) | Typical for Cast Iron |
Thermal conductivity | 23.0 °C | 55 W/(m·K) Show Material materials with Thermal conductivity of 55 W/(m·K) | Typical for Cast Iron |
Chemical properties
Property | Value |
---|---|
Carbon | 3.2 - 4.1 % Show Material materials with Carbon of 3.2 - 4.1 % |
Iron | balance |
Manganese | 0.1 - 1 % Show Material materials with Manganese of 0.1 - 1 % |
Phosphorus | 0.05 % Show Material materials with Phosphorus of 0.05 % |
Silicon | 1.8 - 3 % Show Material materials with Silicon of 1.8 - 3 % |
Sulfur | 0.005 - 0.035 % Show Material materials with Sulfur of 0.005 - 0.035 % |