SAE J158 Grade M3210 Annealed

Want to keep this datasheet? Save it now in your required format

Description

Malleable iron is a cast iron in which the graphite is present as temper carbon nodules, instead of flakes as gray iron or spherulites as in ductile iron. M3210 has good ductility and machinability.

Related Standards

SAE J158

Equivalent Materials

AISI M3210

This material data has been provided by SAE.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.2 - 7.34 g/cm³ Show Material materials with Density of 7.2 - 7.34 g/cm³	Typical for Malleable Cast Iron

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	165 - 180 GPa Show Material materials with Elastic modulus of 165 - 180 GPa	Typical for Malleable Cast Iron
Elongation	23.0 °C	10 % Show Material materials with Elongation of 10 %
Hardness, Brinell	23.0 °C	156 [-] Show Material materials with Hardness, Brinell of 156 [-]
Poisson's ratio	23.0 °C	0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-]	Typical for Malleable Cast Iron
Shear modulus	23.0 °C	64 GPa Show Material materials with Shear modulus of 64 GPa	Typical for Malleable Cast Iron
Tensile strength	23.0 °C	345 MPa Show Material materials with Tensile strength of 345 MPa
Yield strength	23.0 °C	224 MPa Show Material materials with Yield strength of 224 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1E-5 - 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.4E-5 1/K	Typical for Malleable Cast Iron
Melting point		1120 °C Show Material materials with Melting point of 1120 °C	Typical for Cast Iron
Specific heat capacity	23.0 °C	460 - 527 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 527 J/(kg·K)	Typical for Malleable Cast Iron
Thermal conductivity	23.0 °C	51 W/(m·K) Show Material materials with Thermal conductivity of 51 W/(m·K)	Typical for Malleable Cast Iron

Chemical properties

Property	Value
Carbon	2.2 - 2.9 % Show Material materials with Carbon of 2.2 - 2.9 %
Iron	balance
Manganese	0.15 - 1.25 % Show Material materials with Manganese of 0.15 - 1.25 %
Phosphorus	0.02 - 0.1 % Show Material materials with Phosphorus of 0.02 - 0.1 %
Silicon	0.9 - 1.9 % Show Material materials with Silicon of 0.9 - 1.9 %
Sulfur	0.02 - 0.2 % Show Material materials with Sulfur of 0.02 - 0.2 %

Technological properties

Property
Application areas	Steering gear housings, Carriers and Mounting brackets.
Processing history	as agreed