General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.2 g/cm³ Show Material materials with Density of 7.2 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 103 - 118 GPa Show Material materials with Elastic modulus of 103 - 118 GPa | |
Hardness, Brinell | 20.0 °C | 250 - 285 [-] Show Material materials with Hardness, Brinell of 250 - 285 [-] | |
Plane-Strain Fracture Toughnes | 20.0 °C | 15.2 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 15.2 MPa·√m | |
Poisson's ratio | 20.0 °C | 0.26 [-] Show Material materials with Poisson's ratio of 0.26 [-] | |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Tensile strength | 20.0 °C | 155 - 350 MPa Show Material materials with Tensile strength of 155 - 350 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 200.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | |
600.0 °C | 535 J/(kg·K) Show Material materials with Specific heat capacity of 535 J/(kg·K) | ||
Thermal conductivity | 23.0 °C | 55 W/(m·K) Show Material materials with Thermal conductivity of 55 W/(m·K) | Typical for Cast Iron |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 7.3E-7 Ω·m Show Material materials with Electrical resistivity of 7.3E-7 Ω·m |