General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.25 g/cm³ Show Material materials with Density of 7.25 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 108 - 137 GPa Show Material materials with Elastic modulus of 108 - 137 GPa | |
Hardness, Brinell | 20.0 °C | 265 - 285 [-] Show Material materials with Hardness, Brinell of 265 - 285 [-] | |
Plane-Strain Fracture Toughnes | 20.0 °C | 17.7 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 17.7 MPa·√m | |
Poisson's ratio | 20.0 °C | 0.26 [-] Show Material materials with Poisson's ratio of 0.26 [-] | |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Tensile strength | 20.0 °C | 190 - 400 MPa Show Material materials with Tensile strength of 190 - 400 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-5 - 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 - 1.5E-5 1/K | Typical for Grey Cast Iron |
Melting point | 1127 - 1204 °C Show Material materials with Melting point of 1127 - 1204 °C | Typical for Grey Cast Iron | |
Specific heat capacity | 200.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | |
600.0 °C | 535 J/(kg·K) Show Material materials with Specific heat capacity of 535 J/(kg·K) | ||
Thermal conductivity | 23.0 °C | 20 - 80 W/(m·K) Show Material materials with Thermal conductivity of 20 - 80 W/(m·K) | Typical for Grey Cast Iron |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 7E-7 Ω·m Show Material materials with Electrical resistivity of 7E-7 Ω·m |