DIN 1691 Grade GG-35

Want to keep this datasheet? Save it now in your required format


GG-35 used for machine and apparatus pieces with increasing physical properties, for work things machines, compressors. The material is comparable to F 13501 (see to material 50 B, ASTM A 48) and/or US with US F 13502 (see to material 50 B, ASTM A 278 and ASME SA 278) of the USA.

Related Standards

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





20.0 °C

7.3 g/cm³

Show Material materials with Density of 7.3 g/cm³



Elastic modulus

20.0 °C

123 - 143 GPa

Show Material materials with Elastic modulus of 123 - 143 GPa

Hardness, Brinell

20.0 °C

275 - 285 [-]

Show Material materials with Hardness, Brinell of 275 - 285 [-]

Plane-Strain Fracture Toughnes

20.0 °C

20.6 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 20.6 MPa·√m

Poisson's ratio

20.0 °C

0.26 [-]

Show Material materials with Poisson's ratio of 0.26 [-]

Shear modulus

23.0 °C

41 GPa

Show Material materials with Shear modulus of 41 GPa

Typical for Cast Iron

Tensile strength

20.0 °C

210 - 450 MPa

Show Material materials with Tensile strength of 210 - 450 MPa



Melting point

1120 °C

Show Material materials with Melting point of 1120 °C

Typical for Cast Iron

Specific heat capacity

200.0 °C

460 J/(kg·K)

Show Material materials with Specific heat capacity of 460 J/(kg·K)

600.0 °C

535 J/(kg·K)

Show Material materials with Specific heat capacity of 535 J/(kg·K)

Thermal conductivity

23.0 °C

55 W/(m·K)

Show Material materials with Thermal conductivity of 55 W/(m·K)

Typical for Cast Iron



Electrical resistivity

20.0 °C

6.7E-7 Ω·m

Show Material materials with Electrical resistivity of 6.7E-7 Ω·m