EN 13835 Grade GGL-NiCuCr 15 6 3 cast condition

Want to keep this datasheet? Save it now in your required format

Description

GGL NiCuCr 15 6 3 is more corrosion and erosion resistant than GGL-NiCuCr 15 6 2. The material is comparable with UNS F 41000. Application: For pumps, valves, furnace construction units, sleeves, piston ring carriers for guidance metal pistons.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.15 g/cm³

Show Material materials with Density of 7.15 g/cm³

Typical for Grey Cast Iron

Mechanical

PropertyTemperatureValueComment

Compressive yield strength

20.0 °C

860 - 1100 MPa

Show Material materials with Compressive yield strength of 860 - 1100 MPa

Elastic modulus

23.0 °C

92.4 GPa

Show Material materials with Elastic modulus of 92.4 GPa

Typical for Grey Cast Iron

Elongation

20.0 °C

1 %

Show Material materials with Elongation of 1 %

Hardness, Brinell

20.0 °C

150 - 250 [-]

Show Material materials with Hardness, Brinell of 150 - 250 [-]

Poisson's ratio

23.0 °C

0.21 [-]

Show Material materials with Poisson's ratio of 0.21 [-]

Typical for Grey Cast Iron

Shear modulus

23.0 °C

41 GPa

Show Material materials with Shear modulus of 41 GPa

Typical for Cast Iron

Tensile strength

20.0 °C

190 - 240 MPa

Show Material materials with Tensile strength of 190 - 240 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.1E-5 - 1.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.1E-5 - 1.5E-5 1/K

Typical for Grey Cast Iron

Melting point

1127 - 1204 °C

Show Material materials with Melting point of 1127 - 1204 °C

Typical for Grey Cast Iron

Specific heat capacity

23.0 °C

460 J/(kg·K)

Show Material materials with Specific heat capacity of 460 J/(kg·K)

Typical for Grey Cast Iron

Thermal conductivity

23.0 °C

20 - 80 W/(m·K)

Show Material materials with Thermal conductivity of 20 - 80 W/(m·K)

Typical for Grey Cast Iron

Chemical properties

PropertyValue

Carbon

3 %

Show Material materials with Carbon of 3 %

Chromium

2.5 - 3.5 %

Show Material materials with Chromium of 2.5 - 3.5 %

Copper

5.5 - 7.5 %

Show Material materials with Copper of 5.5 - 7.5 %

Manganese

0.5 - 1.5 %

Show Material materials with Manganese of 0.5 - 1.5 %

Nickel

13.5 - 17.5 %

Show Material materials with Nickel of 13.5 - 17.5 %

Silicon

1 - 2.8 %

Show Material materials with Silicon of 1 - 2.8 %