EN 13835 Grade GGL-NiCr 30 3 cast condition

Want to keep this datasheet? Save it now in your required format


GGL NiCr 30 3 is to 800 °C heat and thermal shock-steadily, well corrosion resistant with increased temperatures, particularly erosion steady in saturated steam and salt dredging, middle thermal expansion. The material is comparable to UNS F 41004 with US. Application: For pumps, boiler, valves, filter parts, exit gas lines, turbocharger housings.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

7.15 g/cm³

Show Material materials with Density of 7.15 g/cm³

Typical for Grey Cast Iron



Compressive yield strength

20.0 °C

700 - 910 MPa

Show Material materials with Compressive yield strength of 700 - 910 MPa

Elastic modulus

23.0 °C

92.4 GPa

Show Material materials with Elastic modulus of 92.4 GPa

Typical for Grey Cast Iron


20.0 °C

1 %

Show Material materials with Elongation of 1 %

Hardness, Brinell

20.0 °C

120 - 215 [-]

Show Material materials with Hardness, Brinell of 120 - 215 [-]

Poisson's ratio

23.0 °C

0.21 [-]

Show Material materials with Poisson's ratio of 0.21 [-]

Typical for Grey Cast Iron

Shear modulus

23.0 °C

41 GPa

Show Material materials with Shear modulus of 41 GPa

Typical for Cast Iron

Tensile strength

20.0 °C

190 - 240 MPa

Show Material materials with Tensile strength of 190 - 240 MPa



Coefficient of thermal expansion

23.0 °C

1.1E-5 - 1.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.1E-5 - 1.5E-5 1/K

Typical for Grey Cast Iron

Max service temperature, long

0 - 800 °C

Show Material materials with Max service temperature, long of 0 - 800 °C

Melting point

1127 - 1204 °C

Show Material materials with Melting point of 1127 - 1204 °C

Typical for Grey Cast Iron

Specific heat capacity

23.0 °C

460 J/(kg·K)

Show Material materials with Specific heat capacity of 460 J/(kg·K)

Typical for Grey Cast Iron

Thermal conductivity

23.0 °C

20 - 80 W/(m·K)

Show Material materials with Thermal conductivity of 20 - 80 W/(m·K)

Typical for Grey Cast Iron

Chemical properties



2.5 %

Show Material materials with Carbon of 2.5 %


2.5 - 3.5 %

Show Material materials with Chromium of 2.5 - 3.5 %


0.5 - 0.8 %

Show Material materials with Manganese of 0.5 - 0.8 %


28 - 32 %

Show Material materials with Nickel of 28 - 32 %


1 - 2 %

Show Material materials with Silicon of 1 - 2 %