EN 13835 Grade GGG-NiCr 35 3 cast condition

Want to keep this datasheet? Save it now in your required format

Description

GGG NiCr 35 3 possesses similar characteristics as GGG Ni 35, exhibits however increased heat resistance values, particularly with additive of 1 % molybdenum. The material is comparable to UNS F 43007. Application: Use for gas turbine housing parts, glas pressing die.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.15 g/cm³

Show Material materials with Density of 7.15 g/cm³

Typical for Ductile (Nodular) Cast Iron

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

165 - 180 GPa

Show Material materials with Elastic modulus of 165 - 180 GPa

Typical for Ductile (Nodular) Cast Iron

Elongation

20.0 °C

7 %

Show Material materials with Elongation of 7 %

Hardness, Brinell

20.0 °C

140 - 190 [-]

Show Material materials with Hardness, Brinell of 140 - 190 [-]

Poisson's ratio

23.0 °C

0.26 - 0.31 [-]

Show Material materials with Poisson's ratio of 0.26 - 0.31 [-]

Typical for Ductile (Nodular) Cast Iron

Shear modulus

23.0 °C

63 - 66 GPa

Show Material materials with Shear modulus of 63 - 66 GPa

Typical for Ductile (Nodular) Cast Iron

Tensile strength

20.0 °C

370 - 450 MPa

Show Material materials with Tensile strength of 370 - 450 MPa

Yield strength

20.0 °C

210 - 290 MPa

Show Material materials with Yield strength of 210 - 290 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1E-5 - 1.6E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.6E-5 1/K

Typical for Ductile (Nodular) Cast Iron

Melting point

1150 - 1200 °C

Show Material materials with Melting point of 1150 - 1200 °C

Typical for Ductile (Nodular) Cast Iron

Specific heat capacity

23.0 °C

460 - 502 J/(kg·K)

Show Material materials with Specific heat capacity of 460 - 502 J/(kg·K)

Typical for Ductile (Nodular) Cast Iron

Thermal conductivity

23.0 °C

13 - 42 W/(m·K)

Show Material materials with Thermal conductivity of 13 - 42 W/(m·K)

Typical for Ductile (Nodular) Cast Iron

Chemical properties

PropertyValue

Carbon

2.4 %

Show Material materials with Carbon of 2.4 %

Chromium

2 - 3 %

Show Material materials with Chromium of 2 - 3 %

Manganese

0.5 - 1.5 %

Show Material materials with Manganese of 0.5 - 1.5 %

Nickel

34 - 36 %

Show Material materials with Nickel of 34 - 36 %

Phosphorus

0.08 %

Show Material materials with Phosphorus of 0.08 %

Silicon

1.5 - 3 %

Show Material materials with Silicon of 1.5 - 3 %