DIN 1692 Grade GTS-35-10 not decarburized annealed

Want to keep this datasheet? Save it now in your required format


GTS-35-10, not decarburizing annealed malleable cast iron. The material is comparable to UNS F 22200. Application: for wheel hubs, shift forks, rear axle housing, hydraulic parts, steering housing, planet pinion cage for automatic transmissions, link bodies, shims, casting heads, caps, wing nuts, link bodies.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

7.15 g/cm³

Show Material materials with Density of 7.15 g/cm³

Typical for Ductile (Nodular) Cast Iron



Elastic modulus

23.0 °C

165 - 180 GPa

Show Material materials with Elastic modulus of 165 - 180 GPa

Typical for Ductile (Nodular) Cast Iron


20.0 °C

10 %

Show Material materials with Elongation of 10 %

Hardness, Brinell

20.0 °C

150 [-]

Show Material materials with Hardness, Brinell of 150 [-]

Poisson's ratio

23.0 °C

0.26 - 0.31 [-]

Show Material materials with Poisson's ratio of 0.26 - 0.31 [-]

Typical for Ductile (Nodular) Cast Iron

Shear modulus

23.0 °C

63 - 66 GPa

Show Material materials with Shear modulus of 63 - 66 GPa

Typical for Ductile (Nodular) Cast Iron

Tensile strength

20.0 °C

350 MPa

Show Material materials with Tensile strength of 350 MPa

Yield strength

20.0 °C

200 MPa

Show Material materials with Yield strength of 200 MPa



Coefficient of thermal expansion

23.0 °C

1E-5 - 1.6E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.6E-5 1/K

Typical for Ductile (Nodular) Cast Iron

Melting point

1150 - 1200 °C

Show Material materials with Melting point of 1150 - 1200 °C

Typical for Ductile (Nodular) Cast Iron

Specific heat capacity

23.0 °C

460 - 502 J/(kg·K)

Show Material materials with Specific heat capacity of 460 - 502 J/(kg·K)

Typical for Ductile (Nodular) Cast Iron

Thermal conductivity

23.0 °C

13 - 42 W/(m·K)

Show Material materials with Thermal conductivity of 13 - 42 W/(m·K)

Typical for Ductile (Nodular) Cast Iron

Chemical properties



2.3 - 2.6 %

Show Material materials with Carbon of 2.3 - 2.6 %


0.4 - 0.5 %

Show Material materials with Manganese of 0.4 - 0.5 %


1.2 - 1.5 %

Show Material materials with Silicon of 1.2 - 1.5 %


0.1 - 0.15 %

Show Material materials with Sulfur of 0.1 - 0.15 %