DIN 1692 Grade GTS-70-02 not decarburized annealed

Want to keep this datasheet? Save it now in your required format

Description

GTS-70-02, not decarburizing annealed malleable cast iron. The material is comparable to UNS F 24830. Application: among other things for rail components

Related Standards

Equivalent Materials

Ashby charts

See where DIN 1692 Grade GTS-70-02 not decarburized annealed falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

7.15 g/cm³ at 20 °C

Typical for Ductile (Nodular) Cast Iron

Mechanical

Elastic modulus

E

165 - 180 GPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Elastic modulus of 165 - 180 GPa at 20 °C

Typical for Ductile (Nodular) Cast Iron

Elongation

A

2 % at 20 °C

Show Ductile (Nodular) Cast Iron materials with Elongation of 2 % at 20 °C

Hardness, Brinell

HB

240 - 290 [-] at 20 °C

Show Ductile (Nodular) Cast Iron materials with Hardness, Brinell of 240 - 290 [-] at 20 °C

Poisson's ratio

ν

0.26 - 0.31 [-] at 20 °C

Show Ductile (Nodular) Cast Iron materials with Poisson's ratio of 0.26 - 0.31 [-] at 20 °C

Typical for Ductile (Nodular) Cast Iron

Shear modulus

G

63 - 66 GPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Shear modulus of 63 - 66 GPa at 20 °C

Typical for Ductile (Nodular) Cast Iron

Tensile strength

Rm

700 MPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Tensile strength of 700 MPa at 20 °C

Yield strength

YS

530 MPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Yield strength of 530 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

1E-5 - 1.6E-5 1/K at 20 °C

Typical for Ductile (Nodular) Cast Iron

Specific heat capacity

cp

460 - 527 J/(kg·K) at 20 °C

Typical for Cast Iron

Thermal conductivity

λ

13 - 42 W/(m·K) at 20 °C

Typical for Ductile (Nodular) Cast Iron

Chemical properties

Element

Weight %

Comment

C

2.3 - 2.6 %

Si

1.2 - 1.5 %

Mn

0.4 - 0.5 %

S

0.1 - 0.15 %

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.