DIN 1693-1 Grade GGG-60 cast condition

Want to keep this datasheet? Save it now in your required format

Description

GGG-60, a perlitic-ferritic cast iron material for cast pieces for static and dynamic loading in machines and construction of vehicles as well as in the machine tool manufacture, in civil engineering and energy industry with increased strength and wear-resisting quality, crankshafts, wheel hubs, brake housing, tunnel rings, face plates for centre lathes, camps of high-pressure grease guns, tables for machine tools. The material is comparable to UNS F 33800 of the USA.

Related Standards

Equivalent Materials

Ashby charts

See where DIN 1693-1 Grade GGG-60 cast condition falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

7.15 g/cm³ at 20 °C

Typical for Ductile (Nodular) Cast Iron

Mechanical

Compressive yield strength

R_s

870 MPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Compressive yield strength of 870 MPa at 20 °C

Elastic modulus

E

165 - 180 GPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Elastic modulus of 165 - 180 GPa at 20 °C

Typical for Ductile (Nodular) Cast Iron

Elongation

A

3 % at 20 °C

Show Ductile (Nodular) Cast Iron materials with Elongation of 3 % at 20 °C

Hardness, Brinell

HB

200 - 250 [-] at 20 °C

Show Ductile (Nodular) Cast Iron materials with Hardness, Brinell of 200 - 250 [-] at 20 °C

Poisson's ratio

ν

0.27 - 0.29 [-] at 20 °C

Show Ductile (Nodular) Cast Iron materials with Poisson's ratio of 0.27 - 0.29 [-] at 20 °C

Shear modulus

G

63 - 66 GPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Shear modulus of 63 - 66 GPa at 20 °C

Typical for Ductile (Nodular) Cast Iron

Tensile strength

Rm

600 MPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Tensile strength of 600 MPa at 20 °C

Yield strength

YS

380 MPa at 20 °C

Show Ductile (Nodular) Cast Iron materials with Yield strength of 380 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

1.25E-5 1/K at 100 °C

Hide chart

Specific heat capacity

cp

460 - 527 J/(kg·K) at 20 °C

Typical for Cast Iron

Thermal conductivity

λ

33 W/(m·K) at 100 °C

Unlock all property charts

Chemical properties

Element

Weight %

Comment

C

3.5 - 3.8 %

Si

2 - 3 %

Mn

0.4 %

P

0.1 %

Mg

0.06 - 0.12 %

More

This material data has been provided by WIAM.