General
Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.1 g/cm³ Show Material materials with Density of 7.1 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive yield strength | 20.0 °C | 510 - 850 MPa Show Material materials with Compressive yield strength of 510 - 850 MPa | |
Compressive yield strength, 0.1% | 20.0 °C | 195 MPa Show Material materials with Compressive yield strength, 0.1% of 195 MPa | |
Elastic modulus | 20.0 °C | 78 - 103 GPa Show Material materials with Elastic modulus of 78 - 103 GPa | |
Elongation | 20.0 °C | 0.3 - 0.8 % Show Material materials with Elongation of 0.3 - 0.8 % | |
Flexural strength | 20.0 °C | 273 - 455 MPa Show Material materials with Flexural strength of 273 - 455 MPa | |
Plane-Strain Fracture Toughnes | 20.0 °C | 12 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 12 MPa·√m | |
Poisson's ratio | 20.0 °C | 0.26 [-] Show Material materials with Poisson's ratio of 0.26 [-] | |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Shear strength | 20.0 °C | 170 MPa Show Material materials with Shear strength of 170 MPa | |
Tensile strength | 20.0 °C | 110 - 250 MPa Show Material materials with Tensile strength of 110 - 250 MPa | |
100.0 °C | 150 MPa Show Material materials with Tensile strength of 150 MPa | ||
200.0 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | ||
300.0 °C | 150 MPa Show Material materials with Tensile strength of 150 MPa | ||
400.0 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | ||
500.0 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | ||
600.0 °C | 90 MPa Show Material materials with Tensile strength of 90 MPa | ||
Torsion Strength | 20.0 °C | 204 - 340 MPa Show Material materials with Torsion Strength of 204 - 340 MPa | |
Yield strength Rp0.1 | 20.0 °C | 98 - 165 MPa Show Material materials with Yield strength Rp0.1 of 98 - 165 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 1/K | |
100.0 °C | 1.05E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.05E-5 1/K | ||
200.0 °C | 1.17E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.17E-5 1/K | ||
300.0 °C | 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K | ||
400.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ||
500.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ||
600.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ||
Melting point | 1127 - 1204 °C Show Material materials with Melting point of 1127 - 1204 °C | Typical for Grey Cast Iron | |
Specific heat capacity | 200.0 °C | 460 J/(kg·K) Show Material materials with Specific heat capacity of 460 J/(kg·K) | |
600.0 °C | 535 J/(kg·K) Show Material materials with Specific heat capacity of 535 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 59 W/(m·K) Show Material materials with Thermal conductivity of 59 W/(m·K) | |
100.0 °C | 52.5 W/(m·K) Show Material materials with Thermal conductivity of 52.5 W/(m·K) | ||
200.0 °C | 51 W/(m·K) Show Material materials with Thermal conductivity of 51 W/(m·K) | ||
300.0 °C | 50 W/(m·K) Show Material materials with Thermal conductivity of 50 W/(m·K) | ||
400.0 °C | 49 W/(m·K) Show Material materials with Thermal conductivity of 49 W/(m·K) | ||
500.0 °C | 48.5 W/(m·K) Show Material materials with Thermal conductivity of 48.5 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 6E-7 - 8E-7 Ω·m Show Material materials with Electrical resistivity of 6E-7 - 8E-7 Ω·m |
Technological properties
Property | ||
---|---|---|
Processing methods | sand casting |