Property | Temperature | Value |
---|---|---|
Density | 20.0 °C | 7.2 - 7.5 g/cm³ Show Material materials with Density of 7.2 - 7.5 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 175 - 195 GPa Show Material materials with Elastic modulus of 175 - 195 GPa | |
Hardness, Brinell | 20.0 °C | 150 - 200 [-] Show Material materials with Hardness, Brinell of 150 - 200 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] | Typical for Cast Iron |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Tensile strength | 20.0 °C | 450 MPa Show Material materials with Tensile strength of 450 MPa | |
Yield strength Rp0.2 | 20.0 °C | 270 MPa Show Material materials with Yield strength Rp0.2 of 270 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 20.0 °C | 460 - 500 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 500 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 50 - 63 W/(m·K) Show Material materials with Thermal conductivity of 50 - 63 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 3E-7 - 4E-7 Ω·m Show Material materials with Electrical resistivity of 3E-7 - 4E-7 Ω·m |
Chemical properties
Property | Value |
---|---|
Carbon | 2.3 - 2.6 % Show Material materials with Carbon of 2.3 - 2.6 % |
Manganese | 0.4 - 0.5 % Show Material materials with Manganese of 0.4 - 0.5 % |
Silicon | 1.2 - 1.5 % Show Material materials with Silicon of 1.2 - 1.5 % |
Sulfur | 0.1 - 0.15 % Show Material materials with Sulfur of 0.1 - 0.15 % |