General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7 g/cm³ Show Material materials with Density of 7 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Compressive yield strength | 20.0 °C | 2200 MPa Show Material materials with Compressive yield strength of 2200 MPa |
Elastic modulus | 20.0 °C | 165 GPa Show Material materials with Elastic modulus of 165 GPa |
Elongation | 20.0 °C | 1 % Show Material materials with Elongation of 1 % |
Hardness, Brinell | 20.0 °C | 250 - 480 [-] Show Material materials with Hardness, Brinell of 250 - 480 [-] |
Plane-Strain Fracture Toughnes | 20.0 °C | 50 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 50 MPa·√m |
Poisson's ratio | 20.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] |
Shear modulus | 20.0 °C | 63 GPa Show Material materials with Shear modulus of 63 GPa |
Shear strength | 20.0 °C | 1260 MPa Show Material materials with Shear strength of 1260 MPa |
Tensile strength | 20.0 °C | 1360 - 1400 MPa Show Material materials with Tensile strength of 1360 - 1400 MPa |
Torsion Strength | 20.0 °C | 1260 MPa Show Material materials with Torsion Strength of 1260 MPa |
Yield strength Rp0.2 | 20.0 °C | 1100 MPa Show Material materials with Yield strength Rp0.2 of 1100 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 1.4E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.4E-5 - 1.8E-5 1/K | |
Melting point | 1150 - 1200 °C Show Material materials with Melting point of 1150 - 1200 °C | Typical for Ductile (Nodular) Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 502 J/(kg·K) | Typical for Ductile (Nodular) Cast Iron |
Thermal conductivity | 200.0 °C | 20 - 23 W/(m·K) Show Material materials with Thermal conductivity of 20 - 23 W/(m·K) |