Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.8 g/cm³ Show Material materials with Density of 7.8 g/cm³ | Typical for Duplex Stainless Steel |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 200 GPa Show Material materials with Elastic modulus of 200 GPa | Typical for Duplex Stainless Steel |
Elongation A5 | 23.0 °C | 18 % Show Material materials with Elongation A5 of 18 % | |
Hardness, Brinell | 23.0 °C | 302 [-] Show Material materials with Hardness, Brinell of 302 [-] | |
Hardness, Rockwell C | 23.0 °C | 32 [-] Show Material materials with Hardness, Rockwell C of 32 [-] | |
Hardness, Vickers | 23.0 °C | 320 [-] Show Material materials with Hardness, Vickers of 320 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] | Typical for Duplex Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa Show Material materials with Shear modulus of 77 GPa | Typical for Duplex Stainless Steel |
Tensile strength | 23.0 °C | 620 MPa Show Material materials with Tensile strength of 620 MPa | |
Yield strength Rp0.2 | 23.0 °C | 450 MPa Show Material materials with Yield strength Rp0.2 of 450 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 1/K | Typical for Duplex Stainless Steel |
Max service temperature | 300 °C Show Material materials with Max service temperature of 300 °C | Typical for Duplex Stainless Steel | |
Melting point | 1375 - 1450 °C Show Material materials with Melting point of 1375 - 1450 °C | Typical for Duplex Stainless Steel | |
Specific heat capacity | 23.0 °C | 440 - 502 J/(kg·K) Show Material materials with Specific heat capacity of 440 - 502 J/(kg·K) | Typical for Duplex Stainless Steel |
Thermal conductivity | 23.0 °C | 13 - 30 W/(m·K) Show Material materials with Thermal conductivity of 13 - 30 W/(m·K) | Typical for Duplex Stainless Steel |
Technological properties
Property | ||
---|---|---|
Processing history | solution treated |