General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 7.2 - 7.34 g/cm³ Show Material materials with Density of 7.2 - 7.34 g/cm³ | Typical for Malleable Cast Iron |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 165 - 180 GPa Show Material materials with Elastic modulus of 165 - 180 GPa | Typical for Malleable Cast Iron |
Elongation A5 | 23.0 °C | 2 % Show Material materials with Elongation A5 of 2 % | |
Hardness, Brinell | 23.0 °C | 210 - 260 [-] Show Material materials with Hardness, Brinell of 210 - 260 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] | Typical for Malleable Cast Iron |
Shear modulus | 23.0 °C | 64 GPa Show Material materials with Shear modulus of 64 GPa | Typical for Malleable Cast Iron |
Tensile strength | 23.0 °C | 650 MPa Show Material materials with Tensile strength of 650 MPa | |
Yield strength Rp0.2 | 23.0 °C | 430 MPa Show Material materials with Yield strength Rp0.2 of 430 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-5 - 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1E-5 - 1.4E-5 1/K | Typical for Malleable Cast Iron |
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 527 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 527 J/(kg·K) | Typical for Malleable Cast Iron |
Thermal conductivity | 23.0 °C | 51 W/(m·K) Show Material materials with Thermal conductivity of 51 W/(m·K) | Typical for Malleable Cast Iron |