General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 6.8 - 7.8 g/cm³ Show Material materials with Density of 6.8 - 7.8 g/cm³ | Typical for Cast Iron |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | 23.0 °C | 20 J Show Material materials with Charpy impact energy of 20 J | |
Elastic modulus | 23.0 °C | 152 GPa Show Material materials with Elastic modulus of 152 GPa | Typical for Cast Iron |
Elongation | 23.0 °C | 30 % Show Material materials with Elongation of 30 % | |
Hardness, Brinell | 23.0 °C | 121 - 171 [-] Show Material materials with Hardness, Brinell of 121 - 171 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] Show Material materials with Poisson's ratio of 0.27 [-] | Typical for Cast Iron |
Shear modulus | 23.0 °C | 41 GPa Show Material materials with Shear modulus of 41 GPa | Typical for Cast Iron |
Tensile strength | 23.0 °C | 450 MPa Show Material materials with Tensile strength of 450 MPa | |
Yield strength Rp0.2 | 23.0 °C | 205 MPa Show Material materials with Yield strength Rp0.2 of 205 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Melting point | 1120 °C Show Material materials with Melting point of 1120 °C | Typical for Cast Iron | |
Specific heat capacity | 23.0 °C | 460 - 527 J/(kg·K) Show Material materials with Specific heat capacity of 460 - 527 J/(kg·K) | Typical for Cast Iron |
Thermal conductivity | 23.0 °C | 55 W/(m·K) Show Material materials with Thermal conductivity of 55 W/(m·K) | Typical for Cast Iron |
Chemical properties
Property | Value |
---|---|
Carbon | 2.2 - 2.7 % Show Material materials with Carbon of 2.2 - 2.7 % |
Chromium | 0.2 % Show Material materials with Chromium of 0.2 % |
Manganese | 3.75 - 4.5 % Show Material materials with Manganese of 3.75 - 4.5 % |
Nickel | 21 - 24 % Show Material materials with Nickel of 21 - 24 % |
Phosphorus | 0.08 % Show Material materials with Phosphorus of 0.08 % |
Silicon | 1.5 - 2.5 % Show Material materials with Silicon of 1.5 - 2.5 % |