JIS H5301 Grade ZDC1 as-cast

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by Japanese Industrial Standards.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

7.13 g/cm³

Show Material materials with Density of 7.13 g/cm³

Typical for Zinc

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

105 GPa

Show Material materials with Elastic modulus of 105 GPa

Typical for Zinc

Elongation

23.0 °C

7 %

Show Material materials with Elongation of 7 %

Poisson's ratio

23.0 °C

0.25 [-]

Show Material materials with Poisson's ratio of 0.25 [-]

Typical for Zinc

Shear modulus

23.0 °C

42 GPa

Show Material materials with Shear modulus of 42 GPa

Typical for Zinc

Tensile strength

23.0 °C

324 MPa

Show Material materials with Tensile strength of 324 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.2E-5 - 2.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.8E-5 1/K

Typical for Zinc

Melting point

380 - 420 °C

Show Material materials with Melting point of 380 - 420 °C

Typical for Zinc

Specific heat capacity

23.0 °C

272 - 525 J/(kg·K)

Show Material materials with Specific heat capacity of 272 - 525 J/(kg·K)

Typical for Zinc

Thermal conductivity

23.0 °C

105 - 125 W/(m·K)

Show Material materials with Thermal conductivity of 105 - 125 W/(m·K)

Typical for Zinc

Technological properties

Property
Processing history

as-cast