UNS R31538 Hot Worked

Want to keep this datasheet? Save it now in your required format

Ashby charts

See where UNS R31538 Hot Worked falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

8.4 g/cm³ at 20 °C

Mechanical

Elastic modulus

E

230 GPa at 20 °C

Show Cobalt Chromium Molybdenum materials with Elastic modulus of 230 GPa at 20 °C

Elongation

A

14 % at 20 °C

Show Cobalt Chromium Molybdenum materials with Elongation of 14 % at 20 °C

Tensile strength

Rm

1150 MPa at 20 °C

Show Cobalt Chromium Molybdenum materials with Tensile strength of 1150 MPa at 20 °C

Yield strength

YS

810 MPa at 20 °C

Show Cobalt Chromium Molybdenum materials with Yield strength of 810 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

1.3E-5 1/K at 20 °C

Specific heat capacity

cp

430 J/(kg·K) at 20 °C

Chemical properties

Element

Weight %

Comment

Co

58.7 - 68.9 %

Cr

26 - 30 %

Mo

5 - 7 %

C

0.15 - 0.35 %

Fe

0 - 0.75 %

More

This material data has been provided by MakeItFrom.com.