Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 5.4 g/cm³ Show Material materials with Density of 5.4 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 150 GPa Show Material materials with Elastic modulus of 150 GPa |
Elongation | 23.0 °C | 17 % Show Material materials with Elongation of 17 % |
Tensile strength | 23.0 °C | 1110 MPa Show Material materials with Tensile strength of 1110 MPa |
Yield strength | 23.0 °C | 980 MPa Show Material materials with Yield strength of 980 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-5 1/K | |
Melting point | 1550 - 1815 °C Show Material materials with Melting point of 1550 - 1815 °C | Typical for Titanium Beta Alloy | |
Specific heat capacity | 23.0 °C | 500 J/(kg·K) Show Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 6 - 11 W/(m·K) Show Material materials with Thermal conductivity of 6 - 11 W/(m·K) | Typical for Titanium Beta Alloy |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 2.5 - 3.5 % Show Material materials with Aluminium of 2.5 - 3.5 % |
Carbon | 0 - 0.05 % Show Material materials with Carbon of 0 - 0.05 % |
Hydrogen | 0 - 0.02 % Show Material materials with Hydrogen of 0 - 0.02 % |
Iron | 0 - 0.4 % Show Material materials with Iron of 0 - 0.4 % |
Molybdenum | 14 - 16 % Show Material materials with Molybdenum of 14 - 16 % |
Niobium | 2.2 - 3.2 % Show Material materials with Niobium of 2.2 - 3.2 % |
Nitrogen | 0 - 0.03 % Show Material materials with Nitrogen of 0 - 0.03 % |
Other | 0 - 0.4 % Show Material materials with Other of 0 - 0.4 % |
Oxygen | 0 - 0.17 % Show Material materials with Oxygen of 0 - 0.17 % |
Silicon | 0.15 - 0.25 % Show Material materials with Silicon of 0.15 - 0.25 % |
Titanium | 76 - 81.2 % Show Material materials with Titanium of 76 - 81.2 % |