Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 7.3 g/cm³ Show Material materials with Density of 7.3 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 52 GPa Show Material materials with Elastic modulus of 52 GPa at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] at 23.0 °C | 23.0 °C | Typical for Tin |
Shear modulus | 18 GPa Show Material materials with Shear modulus of 18 GPa at 23.0 °C | 23.0 °C | Typical for Tin |
Tensile strength | 59 MPa Show Material materials with Tensile strength of 59 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.1E-5 1/K at 23.0 °C | 23.0 °C | |
Melting point | 240 °C Show Material materials with Melting point of 240 °C | ||
Specific heat capacity | 220 J/(kg·K) Show Material materials with Specific heat capacity of 220 J/(kg·K) at 23.0 °C | 23.0 °C | |
Thermal conductivity | 52 - 74 W/(m·K) Show Material materials with Thermal conductivity of 52 - 74 W/(m·K) at 23.0 °C | 23.0 °C | Typical for Tin |
Chemical properties
| Property | ||
|---|---|---|
Antimony | 5 - 7.5 % | |
Arsenic | 0 - 0.05 % | |
Copper | 1.5 - 3 % | |
Iron | 0 - 0.02 % | |
Lead | 0 - 0.05 % | |
Tin | 90 - 93 % | |
Zinc | 0 - 5E-3 % |