Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 6 g/cm³ Show Material materials with Density of 6 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 83 GPa Show Material materials with Elastic modulus of 83 GPa at 23.0 °C | 23.0 °C | |
Elongation | 1.6 % Show Material materials with Elongation of 1.6 % at 23.0 °C | 23.0 °C | |
Poisson's ratio | 0.3 [-] Show Material materials with Poisson's ratio of 0.3 [-] at 23.0 °C | 23.0 °C | Typical for Zinc Aluminium |
Tensile strength | 260 MPa Show Material materials with Tensile strength of 260 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 210 MPa Show Material materials with Yield strength of 210 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 2.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 380 °C Show Material materials with Melting point of 380 °C | |
Specific heat capacity | 450 J/(kg·K) Show Material materials with Specific heat capacity of 450 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 120 W/(m·K) Show Material materials with Thermal conductivity of 120 W/(m·K) at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Aluminium | 10.5 - 11.5 % | |
Cadmium | 0 - 6E-3 % | |
Copper | 0.5 - 1.2 % | |
Iron | 0 - 0.08 % | |
Lead | 0 - 6E-3 % | |
Magnesium | 0.02 - 0.03 % | |
Nickel | 0 - 0.02 % | |
Silicon | 0 - 0.06 % | |
Tin | 0 - 3E-3 % | |
Zinc | 87.1 - 89 % |