General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 1.9 g/cm³ Show Material materials with Density of 1.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 45 GPa Show Material materials with Elastic modulus of 45 GPa | |
Elongation | 23.0 °C | 8.3 % Show Material materials with Elongation of 8.3 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Magnesium |
Shear modulus | 23.0 °C | 45 GPa Show Material materials with Shear modulus of 45 GPa | Typical for Magnesium |
Tensile strength | 23.0 °C | 270 MPa Show Material materials with Tensile strength of 270 MPa | |
Yield strength | 23.0 °C | 180 MPa Show Material materials with Yield strength of 180 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.6E-5 1/K |
Melting point | 600 °C Show Material materials with Melting point of 600 °C | |
Specific heat capacity | 23.0 °C | 1040 J/(kg·K) Show Material materials with Specific heat capacity of 1040 J/(kg·K) |
Thermal conductivity | 23.0 °C | 72 W/(m·K) Show Material materials with Thermal conductivity of 72 W/(m·K) |
Chemical properties
Property | Value |
---|---|
Aluminium | 2.4 - 3.6 % Show Material materials with Aluminium of 2.4 - 3.6 % |
Calcium | 0 - 0.04 % Show Material materials with Calcium of 0 - 0.04 % |
Copper | 0 - 0.05 % Show Material materials with Copper of 0 - 0.05 % |
Iron | 0 - 0.05 % Show Material materials with Iron of 0 - 0.05 % |
Magnesium | 93.6 - 97.1 % Show Material materials with Magnesium of 93.6 - 97.1 % |
Manganese | 0.05 - 1 % Show Material materials with Manganese of 0.05 - 1 % |
Nickel | 0 - 5E-3 % Show Material materials with Nickel of 0 - 5E-3 % |
Other | 0 - 0.3 % Show Material materials with Other of 0 - 0.3 % |
Silicon | 0 - 0.1 % Show Material materials with Silicon of 0 - 0.1 % |
Zinc | 0.5 - 1.5 % Show Material materials with Zinc of 0.5 - 1.5 % |