Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 1.9 g/cm³ Show Material materials with Density of 1.9 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 47 GPa Show Material materials with Elastic modulus of 47 GPa | |
Elongation | 23.0 °C | 8.5 % Show Material materials with Elongation of 8.5 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] Show Material materials with Poisson's ratio of 0.29 [-] | Typical for Magnesium |
Shear modulus | 23.0 °C | 45 GPa Show Material materials with Shear modulus of 45 GPa | Typical for Magnesium |
Tensile strength | 23.0 °C | 320 MPa Show Material materials with Tensile strength of 320 MPa | |
Yield strength | 23.0 °C | 230 MPa Show Material materials with Yield strength of 230 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.6E-5 1/K | |
Melting point | 650 °C Show Material materials with Melting point of 650 °C | Typical for Magnesium | |
Specific heat capacity | 23.0 °C | 1050 J/(kg·K) Show Material materials with Specific heat capacity of 1050 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 52 W/(m·K) Show Material materials with Thermal conductivity of 52 W/(m·K) |
Chemical properties
Property | Value |
---|---|
Aluminium | 7.8 - 9.2 % Show Material materials with Aluminium of 7.8 - 9.2 % |
Copper | 0 - 0.05 % Show Material materials with Copper of 0 - 0.05 % |
Iron | 0 - 5E-3 % Show Material materials with Iron of 0 - 5E-3 % |
Magnesium | 89 - 91.9 % Show Material materials with Magnesium of 89 - 91.9 % |
Manganese | 0.12 - 0.5 % Show Material materials with Manganese of 0.12 - 0.5 % |
Nickel | 0 - 5E-3 % Show Material materials with Nickel of 0 - 5E-3 % |
Other | 0 - 0.3 % Show Material materials with Other of 0 - 0.3 % |
Silicon | 0 - 0.1 % Show Material materials with Silicon of 0 - 0.1 % |
Zinc | 0.2 - 0.8 % Show Material materials with Zinc of 0.2 - 0.8 % |