General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | ISO1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 6 % Show Supplier Material materials with Elongation of 6 % | ISO527 |
Flexural modulus | 23.0 °C | 7.5 GPa Show Supplier Material materials with Flexural modulus of 7.5 GPa | ISO178 |
Flexural strength | 23.0 °C | 250 MPa Show Supplier Material materials with Flexural strength of 250 MPa | ISO178 |
Impact strength, Charpy notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO179 |
Impact strength, Charpy unnotched | 23.0 °C | 90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO179 |
Tensile strength | 23.0 °C | 175 MPa Show Supplier Material materials with Tensile strength of 175 MPa | ISO527 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75/A | |
Melting point | 260 - 265 °C Show Supplier Material materials with Melting point of 260 - 265 °C | ISO3146 | |
Flammability | HB UL94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 18 kV/mm Show Supplier Material materials with Dielectric strength of 18 kV/mm | GB/T 1408 |
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm | GB/T1410 |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry, machinery shields, military products, building materials, etc. | |
Fillers | 30% Glass Fiber |